HIPS MOULDING PH-88 CHIMEI granuals Delhi plastic Dealer, Importer

HIPS MOULDING-CHIMEI-PH-88

Add to compare

Processing/Physical Characteristics

Value

Unit

Test Standard

ISO Data

Melt volume-flow rate, MVR

5.5

cm³/10min

ISO 1133

Temperature

200

°C

–

Load

–

Molding shrinkage, parallel

0.6

ISO 294-4, 2577

ASTM Data

Melt Flow Index, MFI

g/10min

ASTM D 1238

Temperature

200

°C

–

Load

–

Mechanical properties

Value

Unit

Test Standard

ISO Data

Yield stress

MPa

ISO 527

Stress at break

MPa

ISO 527

Flexural modulus, 23°C

2100

MPa

ISO 178

Flexural strength

MPa

ISO 178

Charpy notched impact strength, +23°C

kJ/m²

ISO 179/1eA

Charpy notched impact strength, -30°C

6.5

kJ/m²

ISO 179/1eA

Izod notched impact strength, +23°C

kJ/m²

ISO 180/1A

Izod notched impact strength

kJ/m²

ISO 180/1A

Temperature

-30

°C

–

ASTM Data

Tensile Strength at Break

23.5

MPa

ASTM D 638

Flexural Modulus

1931

MPa

ASTM D 790

Flexural Strength

37.2

MPa

ASTM D 790

Rockwell Hardness

L 60

–

ASTM D 785

Izod Impact notched, 1/8 in

98.2

J/m

ASTM D 256

Izod Impact notched, 1/4 in

83.3

J/m

ASTM D 256

Thermal properties

Value

Unit

Test Standard

ISO Data

Temp. of deflection under load, 1.80 MPa

°C

ISO 75-1/-2

Vicat softening temperature, A

°C

ISO 306

Vicat softening temperature, B

°C

ISO 306

Coeff. of linear therm. expansion, parallel

E-6/K

ISO 11359-1/-2

Burning behav. at 1.5 mm nom. thickn.

class

IEC 60695-11-10

Thickness tested

1.5

–

Yellow Card available

yes

–

ASTM Data

UL 94 Flame rating

–

UL 94

Thickness tested

1.5

–

Vicat Temperature

97.8

°C

ASTM D 1525

Electrical properties

Value

Unit

Test Standard

ASTM Data

Arc Resistance

150

ASTM D 495

Other properties	Value	Unit	Test Standard
Density	1030	kg/m³	ISO 1183
Density	1050	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	Value	Unit	Test Standard
Pre-drying – Temperature	80	°C	–
Pre-drying – Time	2 – 3	h	–
Mold temperature	40 – 70	°C	–
Feed temperature	160 – 180	°C

Specification: HIPS MOULDING-CHIMEI-PH-88

ALPHA	C
Group	HIPS
Class	HIPS MOULDING
Color	clear
DENSITY	1.05
GRADE	PH-88
NOTES	PS
Special Properties	Impact resistance grade, Heat resistance grade, high impact
Typical Applications	Daily necessities, toys, electronic products shell
Country	Taiwan
Tds-Name	HIPSChimeiPH-88.pdf
Tds-Url	https://www.materialdatacenter.com/ms/en/tradenames/Polyrex/Chi+Mei+Corporation/POLYREX+PH-88/b4aeee47/545
D-Type	X
Brand	C>CHIMEI