Product Description

LyondellBasell Australia’s Polyproylene grade HP568S is a very high flow homopolymer with a modified molecular weight distribution. HP568S can be used in the melt spinning process for the production of fine denier spunbond non-woven articles.

Regulatory Status

For regulatory compliance information, see Moplen HP568S Product Stewardship Bulletin (PSB) and Safety Data Sheet (SDS).

Status Commercial: Active

Availability Asia-Pacific; Australia and New Zealand

Application Hygiene Film

Market Textile

Processing Method Continuous Filament/Spinning; Spunbond

Attribute Controlled Rheology; Homopolymer; Narrow Molecular Weight Distribution

Typical Properties	Nominal Value	Units	Test Method
Physical
Melt Flow Rate, (230 °C/2.16 kg)	38	g/10 min	ISO 1133-1
Density, (23 °C, Method D)	0.90	g/cm³	ISO 1183
Mechanical
Flexural Modulus	1300	MPa	ISO 178
Tensile Stress at Yield	31	MPa	ISO 527-1, -2

Impact

Notched Izod Impact Strength, (23 °C) 2.2 kJ/m² ISO 180/1A

Hardness

Shore Hardness, (Shore D) 73 ISO 868

Thermal

Vicat Softening Temperature	151	°C	ISO 306
Heat Deflection Temperature B, (0.45 MPa, Unannealed)	70	°C	ISO 75B-1, -2

Specification: PP LAMINATION-BASELL-HP568S

ALPHA	B
Group	PP
Class	PP LAMINATION
GRADE	HP568S
MFI	38
NOTES	PP LAMI
PROCESS	LAMI
Country	Switzerland
Tds-Name	BASELL_HP568S.pdf
Tds-Url	https://sourcechatapp-media.s3.ap-south-1.amazonaws.com/5d3b1334fab74f10438758a9/BASELL_HP568S.pdf
D-Type	S
Brand	B>BASELL