Product Description
Flow, Good; Antistatic
| Physical | Nominal Value | Unit | Test Method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 31 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 27 | cm³/10min | ISO 1133 |
| Molding Shrinkage – Flow (3.00 mm) | 2.0 | % | Internal Method |
| Water Absorption – 60% RH (23°C) | 0.22 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | 2800 | MPa | ISO 527-1/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain
Yield |
8.5 |
% |
ISO 527-2/50 |
| Break | 30 | % | |
| Flexural Modulus 2 | 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 150 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load
0.45 MPa, Unannealed |
156 |
°C |
ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| Melting Temperature | 166 | °C | ISO 11357-3 |
| CLTE
Flow |
1.1E-4 |
cm/cm/°C |
ISO 11359-2 |
| Transverse | 1.1E-4 | cm/cm/°C | |
| Electrical | Nominal Value | Unit | Test Method |
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating (0.8 mm) | HB | UL 94 |
Specification: POM-MITSUBISHI-F30-03
|