| Properties | ISO Test Method | Test Condition | Unit | General | |
| Melt Flow Index | 1133 | 220 ×10KG | ml/10 min | 46 | |
| Melt Flow Index | 1133 | 23 | ml/10 min | 1.17 | |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 38 | |
| 50 mm/min, break | MPa | 29 | |||
| Tensile Elongation | 527 | 50 mm/min | % | 10 | |
| Flexural Strength | 178 | 2 mm/min | MPa | 56 | |
| 2 mm/min | GPa | 1.8 | |||
| Izod Impact Strength | 180/4A | 23 Notched | KJ/m2 | 23 | |
| -30 Notched | KJ/m2 | 10 | |||
| Charpy Impact Strength |
|
23 Notched | KJ/m2 | 24 | |
| -30 Notched | KJ/m2 | 10 | |||
| Vicat Softening Temp. | 306 | 1 Kg,50 | /hr | 93 | |
| 5 Kg,50 | /hr | 79 | |||
| Heat Distortion Temp | 75/A | 1.8 MPa | Unannealed | 76 | |
| 1.8 MPa | Annealed | 84 | |||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8.48 x 10-5 | |
| Flammability | – | UL-94 | – | 2.1mm V-0 | |
| Mold Shrinkage | 294-4 | – | % | 0.3~0.6 | |
| Symbol | 1043 | – | – | >ABS-FR(17)< |
Specification: ABS-CHIMEI-Structure Form PA-765A-UL94-V0
|
User Reviews
Be the first to review “ABS-CHIMEI-Structure Form PA-765A-UL94-V0”
Vendor Information
- No ratings found yet!
There are no reviews yet.