Property
Rheological properties |
Test Condition | Unit | Standard | guide value 1
d.a.m. |
cond. |
C Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80
°C; 600 bar |
% | ISO 294-4 | 0.28 | |
C Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80
°C; 600 bar |
% | ISO 294-4 | 0.47 | |
Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.04 | |
Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.05 | |
Mechanical properties (23 °C/50 % r. h.) | |||||
C Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 20000 | 12000 |
C Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 225 | 145 |
C Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 2.4 | 3.5 |
C Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 90 | 90 |
C Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 90 | 90 |
C Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 16 | 23 |
C Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | 16 | 15 |
Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 80 | 80 |
Izod impact strength | -30 °C | kJ/m² | ISO 180-1U | 80 | 80 |
Izod notched impact strength | 23 °C | kJ/m² | ISO 180-1A | 16 | 20 |
Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | 16 | 15 |
Flexural modulus | 2 mm/min | MPa | ISO 178-A | 19300 | 12800 |
Flexural strength | 2 mm/min | MPa | ISO 178-A | 365 | 235 |
Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 2.8 | 3.6 |
Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 235 | |
C Puncture maximum force | 23 °C | N | ISO 6603-2 | 1250 | 1350 |
C Puncture maximum force | -30 °C | N | ISO 6603-2 | 1100 | 1150 |
C Puncture energy | 23 °C | J | ISO 6603-2 | 3.1 | 4.7 |
C Puncture energy | -30 °C | J | ISO 6603-2 | 2.2 | 2.2 |
Ball indentation hardness | N/mm² | ISO 2039-1 | 255 | 155 | |
Thermal properties | |||||
C Melting temperature | 10 °C/min | °C | ISO 11357-1,-3 | 222 | |
C Temperature of deflection under load | 1.80 MPa | °C | ISO 75-1,-2 | 213 | |
C Temperature of deflection under load | 0.45 MPa | °C | ISO 75-1,-2 | 220 | |
Vicat softening temperature | 50 N; 120 °C/h | °C | ISO 306 | 210 | |
C Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.12 | |
C Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | ISO 11359-1,-2 | 0.75 | |
Electrical properties (23 °C/50 % r. h.) | |||||
C Relative permittivity | 100 Hz | – | IEC 60250 | 5.3 | 11.2 |
C Relative permittivity | 1 MHz | – | IEC 60250 | 4.7 | 5.1 |
C Dissipation factor 100 Hz 10-4 IEC 60250 | 164 | 2149 | |||
C Dissipation factor 1 MHz 10-4 IEC 60250 | 177 | 651 | |||
C Volume resistivity | Ohm·m | IEC 60093 | 5.8E12 | 8E9 |
Specification: NYLON6+GF-LANXESS-BKV 60 H2-0 EF DUS060
|
User Reviews
Be the first to review “NYLON6+GF-LANXESS-BKV 60 H2-0 EF DUS060”
Vendor Information
- No ratings found yet!
There are no reviews yet.