特性 PROPERTIES |
測試方法
ASTM TEST METHOD |
測試條件 TEST CONDITION |
單位 UNIT |
防火級
FLAME RETARDANT |
PA-763 | ||||
熔融指數
Melt Flow Index |
D1238 | 200 ℃, 5 Kg | g/10 min | 2.8 |
220 ℃, 10 Kg | – | |||
比重
Mass Density |
D792 | 23 ℃ | – | 1.19 |
硬度
Hardness |
D785 | – | R Scale | 98 |
拉伸強度 (屈服)
Tensile Strength (Yield) |
D638 | 6 mm/min | Kg/cm2 | 395 |
lb/in2 | 5600 | |||
延伸率
Tensile Elongation |
D638 | 6 mm/min | % | 30 |
彎曲強度
Flexural Strength |
D790 |
2.8 mm/min |
Kg/cm2 | 620 |
lb/in2 | 8800 | |||
彎曲彈性模數
Flexural Modulus |
D790 | 2.8 mm/min | 104 Kg/cm2 | 2.5 |
105 lb/in2 | 3.5 | |||
IZOD 衝擊強度 Izod Impact Strength |
D256 (Notched) |
6.4 mm, 23℃ | Kg-cm/cm | 20 |
ft-lb/in | 3.7 | |||
3.2 mm, 23℃ | Kg-cm/cm | 24 | ||
ft-lb/in | 4.4 | |||
維氏軟化溫度
Vicat Softening Temp. |
D1525 | 1 Kg,50 ℃/hr | ℃ | 104 |
℉ | 219 | |||
熱變形溫度 Heat Distortion Temp. |
D648 |
1.8 MPa Annealed | ℃ | 96 |
℉ | 205 | |||
1.8 MPa Unannealed | ℃ | 85 | ||
℉ | 185 | |||
UL 燃燒等級
UL Flammability |
UL 94 |
– |
– |
1.5 mm V-0
2.5 mm 5VA |
Specification: ABS-CHIMEI-PA-763 -UL94-V0
|