Product Description
Exceed 1327MD is an ethylene 1-hexene copolymer. It produces films which have high modulus whilst retaining good toughness. Additionally, Exceed 1327MD is fully formulated with slip and antiblock, giving a versatile ready-to-use polymer for applications such as form fill and seal. TnPP is not intentionally added to Exceed 1327MD.
| Resin Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Density / Specific Gravity |
0.927 |
g/cm³ |
0.927 |
g/cm³ |
ASTM D792 |
| Melt Index (190°C/2.16 kg) |
1.3 |
g/10 min |
1.3 |
g/10 min |
ASTM D1238 |
| Peak Melting Temperature |
253 |
°F |
123 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Thermal |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Vicat Softening Temperature |
241 |
°F |
116 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Film Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Tensile Strength at Yield MD |
1900 |
psi |
13 |
MPa |
ASTM D882 |
| Tensile Strength at Yield TD |
2100 |
psi |
14 |
MPa |
ASTM D882 |
| Tensile Strength at Break MD |
6800 |
psi |
47 |
MPa |
ASTM D882 |
| Tensile Strength at Break TD |
5700 |
psi |
39 |
MPa |
ASTM D882 |
| Elongation at Break MD |
560 |
% |
560 |
% |
ASTM D882 |
| Elongation at Break TD |
620 |
% |
620 |
% |
ASTM D882 |
| Secant Modulus MD – 1% Secant |
45000 |
psi |
310 |
MPa |
ASTM D882 |
| Secant Modulus TD – 1% Secant |
48000 |
psi |
330 |
MPa |
ASTM D882 |
| Dart Drop Impact |
140 |
g |
140 |
g |
ASTM D1709A |
| Elmendorf Tear Strength MD |
190 |
g |
190 |
g |
ASTM D1922 |
| Elmendorf Tear Strength TD |
450 |
g |
450 |
g |
ASTM D1922 |
| Puncture Force |
9 |
lbf |
38 |
N |
ExxonMobil Method |
| Puncture Energy |
15 |
in·lb |
1.7 |
J |
ExxonMobil Method |
| |
|
|
|
|
|
| Optical Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Gloss (45°) |
25 |
|
25 |
|
ASTM D2457 |
| Haze |
26 |
% |
26 |
% |
ASTM D1003 |