ABS MOULDING-LG-HI121H
Properties
| Physical
Specific Gravity |
Test Condition | Test Method
ASTM D792 |
Unit
– |
Typical Value
1.04 |
| Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.4~0.7 | |
| Melt Flow Rate | 220℃/10kg | ASTM D1238 | g/10min | 23 |
Mechanical
| Tensile Strength, 3.2mm
@ Yield |
50mm/min |
ASTM D638 |
kg/cm2 |
520 |
| Tensile Elongation, 3.2mm
@ Break |
50mm/min |
ASTM D638 |
% |
30 |
| Tensile Modulus, 3.2mm | 1mm/min | ASTM D638 | kg/cm2 | 22,600 |
| Flexural Strength, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 800 |
| Flexural Modulus, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 28,000 |
| IZOD Impact Strength, 6.4mm
(Notched) |
23℃ |
ASTM D256 |
kg·cm/cm |
20 |
| -30℃ | kg·cm/cm | 8 | ||
| IZOD Impact Strength, 3.2mm
(Notched) |
23℃ |
ASTM D256 |
kg·cm/cm |
23 |
| -30℃ | kg·cm/cm | 8 | ||
| Rockwell Hardness | R-Scale | ASTM D785 | – | 110 |
Thermal
| Heat Deflection Temperature, 6.4mm
(Unannealed) |
18.6kg |
ASTM D648 |
℃ |
86 |
| 4.6kg | ℃ | 90 | ||
| Vicat Softening Temperature | ASTM D1525 | |||
| 5kg, 50℃/h | ℃ | 94 | ||
| Flammability | UL94 | HB | ||
| Relative Temperature Index | UL 746B | |||
| Electrical | ℃ | 60 | ||
| Mechanical with Impact | ℃ | 60 | ||
| Mechanical without Impact | ℃ | 60 |
Specification: ABS MOULDING-LG-HI121H
|