LDPE 1022 FN 24 is a low density polyethylene made by a high pressure process without antioxidant.LDPE 1022 FN 24 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as bags, lamination and coextrusion film.Information provided by Total Petrochemicals.
Physical Properties | Metric | English | Comments |
Specific Gravity | 0.923 g/cc | 0.923 g/cc | ISO 1183 |
Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
25.0 – 150 microns | 0.984 – 5.91 mil | possible range, depending on extrusion conditions | |
Melt Flow |
2.3 g/10 min
@Load 2.16 kg, Temperature 190 °C |
2.3 g/10 min
@Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO 527-3 |
Film Tensile Strength at Yield, TD | 11.5 MPa | 1670 psi | ISO 527-3 |
Film Elongation at Break, MD | 360 % | 360 % | ISO 527-3 |
Film Elongation at Break, TD | 630 % | 630 % | ISO 527-3 |
Elmendorf Tear Strength, MD | 7.60 g/micron | 193 g/mil | ISO 6383-2 |
Elmendorf Tear Strength, TD | 6.30 g/micron | 160 g/mil | ISO 6383-2 |
Dart Drop Test | 95.0 g | 0.209 lb | ISO 7765-1 |
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
Thermal Properties | Metric | English | Comments |
Melting Point | 109 °C | 228 °F | ISO 11357 |
Vicat Softening Point | 94.0 °C | 201 °F | ISO 306 |
Optical Properties | Metric | English | Comments |
Haze | 7.0 % | 7.0 % | ISO 14782 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 150 – 190 °C | 302 – 374 °F |
Specification: LD FILM-TOTAL-1022FN24
|