LL FILM-SASOL-HF1810PX
@ Plastic Dealer Ask owner
Features
- LLDPE Hexene copolymer
- Outstanding mechanical properties and processability
- Good heat sealing range
Applications
- General purpose packaging
- Heavy duty bags and high speed thin films
- Blown stretch film
- Blending into LDPE
| Typical properties (not to be construed as specifications) | Value (English) | Value (SI) | Method | |
|
Resin Properties |
Melt Index (190°C/2.16kg) | 1.0 g/10min | 1.0 g/10min | ASTM D1238 |
| Density | 0.922 g/cm3 | 0.922 g/cm3 | ASTM D792 | |
| Base Density(1) | 0.918 g/cm3 | 0.918 g/cm3 | Sasol Method | |
|
Film Properties |
Tensile strength at yield MD | 2330 psi | 16.0 MPa | ASTM D882 |
| Tensile strength at yield TD | 2240 psi | 15.4 MPa | ASTM D882 | |
| Tensile strength at break MD | 6500 psi | 44.8 MPa | ASTM D882 | |
| Tensile strength at break TD | 5000 psi | 34.5 MPa | ASTM D882 | |
| Tensile Elongation at break MD | 500 % | 500 % | ASTM D882 | |
| Tensile Elongation at break TD | 700 % | 700 % | ASTM D882 | |
| 1% Secant Modulus MD | 38000 psi | 262 MPa | ASTM D882 | |
| 1% Secant Modulus TD | 37000 psi | 255 MPa | ASTM D882 | |
| Elmendorf Tear Strength MD | 310 g/mil | 310 g/25.4 µm | ASTM D1922 | |
| Elmendorf Tear Strength TD | 800 g/mil | 800 g/25.4 µm | ASTM D1922 | |
| Dart Drop Impact Strength (F50) | 200 g/mil | 200 g/25.4 µm | ASTM D1709A | |
| Haze | 16% | 16% | ASTM D1003 | |
| Gloss (45°) | 45% | 45% | ASTM D2457 | |
Specification: LL FILM-SASOL-HF1810PX
|