| 71601W is a LLDPE blown film grade produced by the Spherilene Technology with controlled morphology, excellent processability & mechanical properties
This grade can be used in General Purpose Adhesive Lamination film 71601W is without slip or antiblocking additives BIS Designation Code: IS 7328-2B-FBE-BDA |
|||
| Property | Test Method | Unit | Nominal Value |
| Melt Flow Index (2.16 kg, 190°C) | ASTM D1238,
IS 13360 (Part 4/Sec 1) |
g/10 min |
1.0 |
| Melt Flow Index (5 kg, 190°C) | 2.6 | ||
| Melt Flow Index (21.6 kg, 190°C) | ASTM D1238 | g/10 min | 23 |
| Density (23°C) | ASTM D1505,
IS 13360 (Part 3/Sec 11) |
g/cm3 | 0.920 |
| DSC Melting Temperature | ASTM D3418 | °C | 125 |
| Film Property ** | |||
| Tensile Strength at Yield MD |
ASTM D882 (500 mm/min) |
MPa | 10 |
| Tensile Strength at Yield TD | MPa | 10 | |
| Tensile Strength at Break MD | MPa | 25 | |
| Tensile Strength at Break TD | MPa | 16 | |
| Elongation at Break MD | % | 650 | |
| Elongation at Break TD | % | 750 | |
| Elmendorf Tear Strength MD |
ASTM D1922 |
g | 150 |
| Elmendorf Tear Strength TD | g | 400 | |
| Dart Impact Strength, F50 (38 mm Dart, 66 cm Height) | ASTM D1709A | g/µm | 4.0 |
| Gloss at 60° | ASTM D2457 | GU | 76 |
| Suggested Processing Conditions | |||
| Barrel Temperature | 180 – 200 °C | ||
| Melt Temperature | 190 – 210 °C | ||
| Blow up Ratio | 2.0 – 3.0 | ||
| Die Gap | 2.0 – 2.5 mm | ||
Specification: LL FILM-HALDIA-71601W
|