Product Description
Exceed™ XP 6026 is an eXtreme Performance linear low density polyethylene 1-hexene copolymer that is especially designed to have high melt strength and superior tensile, impact, and puncture properties. The combination of high toughness, melt stability and good sealing performance makes this grade a versatile blown film resin. TnPP is not intentionally added to Exceed™ XP 6026. Exceed™ XP 6026 – when eXtreme Performance matters.
| Resin Properties | Typical Value | (English) Typical Value | (SI) | Test Based On |
| Density / Specific Gravity | 0.916 | g/cm³ 0.916 | g/cm³ | ASTM D792 |
| Melt Index (190°C/2.16 kg) | 0.20 | g/10 min 0.20 | g/10 min | ASTM D1238 |
| Peak Melting Temperature | 230 | °F 110 | °C | ExxonMobil Method |
| Film Properties | Typical Value | (English) Typical Value | (SI) | Test Based On |
| Tensile Strength at Yield MD | 1300 | psi 8.9 | MPa | ASTM D882 |
| Tensile Strength at Yield TD | 1400 | psi 9.9 | MPa | ASTM D882 |
| Tensile Strength at Break MD | 9400 | psi 70 | MPa | ASTM D882 |
| Tensile Strength at Break TD | 9700 | psi 70 | MPa | ASTM D882 |
| Elongation at Break MD | 390 | % 390 | % | ASTM D882 |
| Elongation at Break TD | 640 | % 640 | % | ASTM D882 |
| Secant Modulus MD – 1% Secant | 26000 | psi 180 | MPa | ASTM D882 |
| Secant Modulus TD – 1% Secant | 32000 | psi 220 | MPa | ASTM D882 |
| Dart Drop Impact 2 | 680 | g 680 | g | ASTM D1709 |
| Elmendorf Tear Strength MD | 60 | g 60 | g | ASTM D1922 |
| Elmendorf Tear Strength TD | 400 | g 400 | g | ASTM D1922 |
| Puncture Force | 15 | lbf 67 | N | ExxonMobil Method |
| Puncture Energy | 43 | in·lb 4.8 | J | ExxonMobil Method |
| Optical Properties | Typical Value | (English) Typical Value | (SI) | Test Based On |
| Gloss (45°) | 44 | 44 | ASTM D2457 | |
| Haze | 12 | % 12 | % | ASTM D1003 |
Specification: LL FILM-ExxonMobil-6026ML
|