Product Description
FT5236 is a Low Density Polyethylene for Film Extrusion. Tubular Technology. Includes Anti-block and Medium Slip additives.
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Density | 0.923 g/cm³ | 0.923 g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 g/10 min | 0.75 g/10 min | ISO 1133 |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Coefficient of Friction
vs. Itself – Dynamic, Blown Film |
0.20 |
0.20 |
ISO 8295 |
| Films | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Film Thickness – Tested | 1.6 mil | 40 µm | |
| Secant Modulus
MD : 1.6 mil (40 µm), Blown Film |
33400 psi |
230 MPa |
ASTM D882A |
| TD : 1.6 mil (40 µm), Blown Film | 37700 psi | 260 MPa | |
| Tensile Strength
MD : 1.6 mil (40 µm), Blown Film |
3920 psi |
27.0 MPa |
ISO 527-3 |
| TD : 1.6 mil (40 µm), Blown Film | 3480 psi | 24.0 MPa | |
| Tensile Elongation
MD : Break, 1.6 mil (40 µm), Blown Film |
250 % |
250 % |
ISO 527-3 |
| TD : Break, 1.6 mil (40 µm), Blown Film | 550 % | 550 % | |
| Dart Drop Impact
1.6 mil (40 µm), Blown Film |
120 g |
120 g |
ISO 7765-1 |
| Elmendorf Tear Strength
MD : 1.6 mil (40 µm), Blown Film |
0.90 lbf |
4.0 N |
ISO 6383-2 |
| TD : 1.6 mil (40 µm), Blown Film | 0.45 lbf | 2.0 N | |
| Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Multi-Axial Instrumented Impact Energy
0.00157 in (0.0400 mm), Blown Film, Total Penetration Energy |
1.84 ft·lb |
2.50 J |
ISO 6603-2 |
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Melting Temperature | 234 °F | 112 °C | ISO 11357-3 |
| Optical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Gloss (1.57 mil (40.0 µm), Blown Film) | 85 | 85 | ASTM D2457 |
| Haze (1.57 mil (40.0 µm), Blown Film) | 8.0 % | 8.0 % | ASTM D1003 |
| Extrusion | Nominal Value (English) | Nominal Value (SI) | |
| Melt Temperature | 320 to 374 °F | 160 to 190 °C | |
Specification: LD FILM-BOROUGE-FT5236
|