| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.916 | g/cm³ | 0.916 | g/cm³ | ASTM D792 |
| Base Density 1 | 0.916 | g/cm³ | 0.916 | g/cm³ | Dow Method |
| Melt Mass-Flow Rate (190°C/2.16 kg) | 3.0 | g/10 min | 3.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 0.94 | mil | 24 | µm | |
| Film Puncture Resistance (0.94 mil (24 µm)) | 134 | ft·lb/in³ | 11.1 | J/cm³ | Dow Method |
| Secant Modulus
2% Secant, MD : 0.94 mil (24 µm) |
28100 |
psi |
194 |
MPa |
ASTM D882 |
| 2% Secant, TD : 0.94 mil (24 µm) | 25200 | psi | 174 | MPa | |
| Tensile Strength
MD : Yield, 0.94 mil (24 µm) |
4870 |
psi |
33.6 |
MPa |
ASTM D882 |
| TD : Yield, 0.94 mil (24 µm) | 2630 | psi | 18.1 | MPa | |
| MD : Break, 0.94 mil (24 µm) | 870 | psi | 6.00 | MPa | |
| TD : Break, 0.94 mil (24 µm) | 754 | psi | 5.20 | MPa | |
| Tensile Elongation
MD : Break, 0.94 mil (24 µm) |
560 |
% |
560 |
% |
ASTM D882 |
| TD : Break, 0.94 mil (24 µm) | 870 | % | 870 | % | |
| Dart Drop Impact (0.94 mil (24 µm)) | 50 | g | 50 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD : 0.94 mil (24 µm) |
52 |
g |
52 |
g |
ASTM D1922 |
| TD : 0.94 mil (24 µm) | 260 | g | 260 | g | |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (45°, 0.940 mil (23.9 µm)) | 93 | 93 | ASTM D2457 | ||
| Haze (0.940 mil (23.9 µm)) | 0.94 | % | 0.94 | % | ASTM D1003 |
Specification: LL FILM-DOW-1050P
|