Product Description
A medium viscosity grade for general injection molding. It was reinforced glass fiber, and so suitable for parts requiring very high stiffness, fatigue resistance, creep resistance, and heat resistance.
| Physical
— — |
Nominal Value (English)
1.50 1.50 g/cm³ |
Nominal Value (SI)
1.50 g/cm³ 1.50 g/cm³ |
Test Method Specific Gravity
ASTM D792 ISO 1183 |
| Melt Mass-Flow Rate (MFR) 190°C/2.16 kg |
12 g/10 min |
12 g/10 min |
ASTM D1238 |
| — | 12 g/10 min | 12 g/10 min | ISO 1133 |
| Molding Shrinkage – Flow (0.0787 in (2.00 mm)) | 8.0E-3 in/in | 0.80 % | ASTM D955 |
| Water Absorption
Equilibrium, 73°F (23°C), 60% RH |
0.20 % |
0.20 % |
ASTM D570 |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Tensile Strength Yield, 73°F (23°C) |
16100 psi |
111 MPa |
ASTM D638 |
| Break, 73°F (23°C) | 17400 psi | 120 MPa | ISO 527-2 |
| Tensile Elongation Break, 73°F (23°C) |
3.0 % |
3.0 % |
ASTM D638 |
| Break, 73°F (23°C) | 3.6 % | 3.6 % | ISO 527-2 |
| Flexural Modulus 73°F (23°C) |
777000 psi |
5350 MPa |
ASTM D790 |
| 73°F (23°C) | 754000 psi | 5200 MPa | ISO 178 |
| Flexural Strength 73°F (23°C) |
22800 psi |
157 MPa |
ASTM D790 |
| 73°F (23°C) | 25400 psi | 175 MPa | ISO 178 |
| Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Charpy Notched Impact Strength | 3.3 ft·lb/in² | 7.0 kJ/m² | ISO 179/1eA |
| Notched Izod Impact (0.126 in (3.20 mm)) | 1.3 ft·lb/in | 69 J/m | ASTM D256 |
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Deflection Temperature Under Load
264 psi (1.8 MPa), Unannealed |
327 °F |
164 °C |
ASTM D648 |
| Peak Melting Temperature | 329 °F | 165 °C | ASTM D3418 |
| Electrical | Nominal Value (English) | Nominal Value (SI) | Test Method |
Specification: POM-Kepital-Kepital FG2015
|