| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.920 | g/cm³ | 0.920 | g/cm³ | ASTM D792 |
| Base Density | 0.920 | g/cm³ | 0.920 | g/cm³ | Dow Method 1 |
| Melt Index (190°C/2.16 kg) | 4.0 | g/10 min | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 0.91 | mil | 23 | µm | |
| Film Puncture Energy (0.91 mil (23 µm)) | 1180 | in·lb | 133 | J | |
| Film Puncture Force (0.91 mil (23 µm)) | 6.97 | lbf | 31.0 | N | |
| Tensile Strength
MD : Yield, 0.91 mil (23 µm) |
870 |
psi |
6.00 |
MPa |
ASTM D882 |
| TD : Yield, 0.91 mil (23 µm) | 870 | psi | 6.00 | MPa | |
| MD : Break, 0.91 mil (23 µm) | 5220 | psi | 36.0 | MPa | |
| TD : Break, 0.91 mil (23 µm) | 3630 | psi | 25.0 | MPa | |
| Tensile Elongation
MD : Break, 0.91 mil (23 µm) |
400 |
% |
400 |
% |
ASTM D882 |
| TD : Break, 0.91 mil (23 µm) | 680 | % | 680 | % | |
| Dart Drop Impact (0.91 mil (23 µm)) | 110 | g | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD : 0.91 mil (23 µm) |
150 |
g |
150 |
g |
ASTM D1922 |
| TD : 0.91 mil (23 µm) | 450 | g | 450 | g | |
| Film Stretch Performace – Max Elongation
0.9 mil (23.0 µm) |
350 |
% |
350 |
% |
Dow Method |
| Film Stretch Performace – Max Stretch Force
0.9 mil (23.0 µm) |
36000 |
g |
36000 |
g |
Dow Method |
| Additional Information |
Specification: LL FILM-DOW-2606GC
|