ABS MOULDING-LG-HI121
Product Description
- Well balanced mechanical properties
Application
Electric/electronic products, miscellaneous goods
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Density / Specific Gravity 4 | 1.04 | 1.04 g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Molding Shrinkage – Flow
73°F (23°C), 0.126 in (3.20 mm) |
4.0E-3 to 7.0E-3 in/in |
0.40 to 0.70 % |
ASTM D955 |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Tensile Modulus 5
73°F (23°C), 0.126 in (3.20 mm) |
312000 psi |
2150 MPa |
ASTM D638 |
| Tensile Strength 5
Yield, 73°F (23°C), 0.126 in (3.20 mm) |
6530 psi |
45.0 MPa |
ASTM D638 |
| Tensile Elongation 5
Yield, 73°F (23°C), 0.126 in (3.20 mm) |
> 5.0 % |
> 5.0 % |
ASTM D638 |
| Break, 73°F (23°C), 0.126 in (3.20 mm) | > 10 % | > 10 % | |
| Flexural Modulus 6
73°F (23°C), 0.126 in (3.20 mm) |
355000 psi |
2450 MPa |
ASTM D790 |
| Flexural Strength 6
73°F (23°C), 0.126 in (3.20 mm) |
10600 psi |
73.0 MPa |
ASTM D790 |
| Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Notched Izod Impact
-22°F (-30°C), 0.126 in (3.20 mm) |
2.8 ft·lb/in |
150 J/m |
ASTM D256 |
| -22°F (-30°C), 0.252 in (6.40 mm)
73°F (23°C), 0.126 in (3.20 mm) 73°F (23°C), 0.252 in (6.40 mm) |
2.8 ft·lb/in
6.1 ft·lb/in 6.1 ft·lb/in |
150 J/m
320 J/m 320 J/m |
|
| Hardness | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Rockwell Hardness (R-Scale) | 108 | 108 | ASTM D785 |
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Deflection Temperature Under Load
264 psi (1.8 MPa), Unannealed, 0.252 in (6.40 mm) |
185 °F |
85.0 °C |
ASTM D648 |
| Vicat Softening Temperature | 199 °F | 93.0 °C | ASTM D1525 7 |
| RTI Elec | 203 °F | 95.0 °C | UL 746 |
| RTI Imp | 203 °F | 95.0 °C | UL 746 |
| RTI Str | 203 °F | 95.0 °C | UL 746 |