| 72307E is a LLDPE produced by the Spherilene Technology
72307E can be used in Extrusion Coating on HDPE Woven Fabric, Aluminium Foil, Jute, Paper & Allied Substrates The precise morphological control achieved during polymerization confers superior processability and improved performance properties not available in conventional LLDPE BIS Designation Code: IS 7328-2B-HB-CDD |
|||
| Property | Test Method | Unit | Nominal Value |
| Melt Flow Index (2.16 kg, 190°C) |
ASTM D1238, IS 13360 (Part 4/Sec 1) |
g/10 min |
7.0 |
| Melt Flow Index (5 kg, 190°C) | 19.0 | ||
| Melt Flow Index (21.6 kg, 190°C) | ASTM D1238 | g/10 min | 165 |
| Density (23°C) | ASTM D1505,
IS 13360 (Part 3/Sec 11) |
g/cm3 | 0.926 |
| Physical Property | |||
| Tensile Strength at Break |
ASTM D638 (50 mm/min) |
MPa | 18 |
| Elongation at Break | % | 300 | |
| Notched Izod Impact Strength (23°C) | ASTM D256A | J/m | 500 |
| Flexural Modulus | ASTM D790A | MPa | 300 |
| Vicat Softening Point (10 N) | ASTM D1525 | °C | 102 |
| DSC Melting Temperature | ASTM D3418 | °C | 126 |
| Suggested Processing Conditions | |||
| Barrel Temperature | 200 – 270 °C | ||
| Die Temperature | 250 – 280 °C | ||