Product Description
DOw LDPeTM 582e Polyethylene Resin can be readily extruded using conventional blown film techniques utilising melt temperatures between 150 and 170°C. DOw LDPe 582e Polyethylene Resin, when properly fabricated, shows good mechanical properties and high optical properties. It shows very good drawdown properties and excellent processability. This product contains slip and antiblock additives.
| Physical | Nominal Value Unit | Test Method |
| Specific Gravity | 0.923 g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 g/10 min | ISO 1133 |
| Mechanical | Nominal Value Unit | Test Method |
| Coefficient of Friction | 0.16 to 0.20 | ASTM D1894 |
| Films | Nominal Value Unit | Test Method |
| Film Thickness – Tested | 50 µm | |
| Secant Modulus
2% Secant, MD: 50 µm |
190 MPa |
ASTM D882 |
| 2% Secant, TD: 50 µm | 175 MPa | |
| Tensile Strength
MD: yield, 50 µm |
9.00 MPa |
ASTM D882 |
| TD: yield, 50 µm
MD: Break, 50 µm TD: Break, 50 µm |
9.00 MPa
17.0 MPa 15.0 MPa |
|
| Tensile elongation
MD: Break, 50 µm |
450 % |
ASTM D882 |
| TD: Break, 50 µm | 650 % | |
| Dart Drop Impact (50 µm) | 120 g | ASTM D1709A |
| elmendorf Tear Strength
MD: 50 µm |
500 g |
ASTM D1922 |
| TD: 50 µm | 400 g | |
| Thermal | Nominal Value Unit | Test Method |
| Vicat Softening Temperature | 93.0 °C | ISO 306/A |
| Optical | Nominal Value Unit | Test Method |
| Gloss (20°, 50.0 µm) | 70 | ASTM D2457 |
| Haze (50.0 µm) | 7.0 % | ASTM D1003 |
Specification: LD BLOW-DOW-582E
|