| General |
|
| Material Status |
• Commercial: Active |
|
|
| Availability |
• Asia Pacific |
• Europe |
• North America |
| Features |
• General Purpose |
• High Flow |
|
| Uses |
• Blending |
• Electrical/Electronic Applications |
• Thin-walled Packaging |
| RoHS Compliance |
• RoHS Compliant |
|
|
| Forms |
• Pellets |
|
|
| Processing Method |
• Injection Molding |
|
|
| Physical |
Nominal Value Unit |
Test Method |
| Specific Gravity |
1.04 g/cm³ |
ASTM D792 ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) |
10 g/10 min |
ASTM D1238 ISO 1133 |
| Molding Shrinkage – Flow (23°C) |
0.30 to 0.50 % |
Internal Method |
| Mechanical |
Nominal Value Unit |
Test Method |
| Tensile Modulus (23°C) |
1670 MPa |
ASTM D638 ISO 527-2 |
| Tensile Strength |
|
|
| Yield, 23°C |
39.2 MPa |
ASTM D638 |
| Yield, 23°C |
39.0 MPa |
ISO 527-2 |
| Tensile Elongation (Break, 23°C) |
2.1 % |
ASTM D638 ISO 527-2 |
| Flexural Modulus (23°C) |
3240 MPa |
ASTM D790 ISO 178 |
| Flexural Strength |
|
|
| 23°C |
68.6 MPa |
ASTM D790 |
| 23°C |
69.0 MPa |
ISO 178 |
| Impact |
Nominal Value Unit |
Test Method |
| Notched Izod Impact |
|
|
| 23°C, 6.35 mm |
18.0 J/m |
ISO 180 |
| 23°C, 6.35 mm |
17.7 J/m |
ASTM D256 |
| Thermal |
Nominal Value Unit |
Test Method |
| Deflection Temperature Under Load |
|
|
| 1.8 MPa, Unannealed, 3.18 mm |
82.0 °C |
ASTM D648 |
| 1.8 MPa, Unannealed, 3.18 mm Span |
82.0 °C |
ISO 75-2/A |
| Vicat Softening Temperature |
|
|
|
| — |
88.0 °C |
ASTM D1525 2 |
| — |
135 °C |
ISO 306/A |
| Flammability |
Nominal Value Unit |
Test Method |
| Flame Rating – UL (1.59 mm, Natural Color) |
HB |
UL 94 |
| UL File Number |
E162823 |
|
| Additional Information |
Nominal Value Unit |
|
| Residual Monomer |
< 700 ppm |
|
| Notched Izod Impact Strength, ISO 180, 23°C, 0.25 in: 18 J/m Residual Monomer: 700 ppm max |
|
|