Rheological propertie
| Melt volume-flow rate |
260 °C/ 5 kg |
cm³/10 min |
ISO 1133 |
18 |
| Melt viscosity |
1000 s-1/ 260 °C |
Pa·s |
b.o. ISO 11443-A |
200 |
| Molding shrinkage, parallel |
150x105x3 mm/ 260 °C / MT 80 °C |
% |
b.o. ISO 2577 |
0.5 – 0.7 |
| Molding shrinkage, normal |
150x105x3 mm/ 260 °C / MT 80 °C |
% |
b.o. ISO 2577 |
0.5 – 0.7 |
Mechanical properties (23 °C/50 % r. h.
| Tensile modulus |
1 mm/min |
MPa |
ISO 527-1,-2 |
2350 |
| Yield stress |
50 mm/min |
MPa |
ISO 527-1,-2 |
54 |
| Yield strain |
50 mm/min |
% |
ISO 527-1,-2 |
4.4 |
| Stress at break |
50 mm/min |
MPa |
ISO 527-1,-2 |
47 |
| Strain at break |
50 mm/min |
% |
b.o. ISO 527-1,-2 |
> 50 |
| Flexural modulus |
2 mm/min |
MPa |
ISO 178 |
2350 |
| Flexural stress at 3.5 % strain |
2 mm/min |
MPa |
ISO 178 |
73 |
| Flexural strength |
2 mm/min |
MPa |
ISO 178 |
84 |
| Izod impact strength |
23 °C |
kJ/m² |
ISO 180/U |
N |
| Izod impact strength |
-30 °C |
kJ/m² |
ISO 180/U |
N |
| Izod notched impact strength |
23 °C |
kJ/m² |
ISO 180/A |
48 |
| Izod notched impact strength |
-30 °C |
kJ/m² |
ISO 180/A |
35 |
| Charpy notched impact strength |
23 °C |
kJ/m² |
ISO 179/1eA |
50 |
| Charpy notched impact strength |
-30 °C |
kJ/m² |
ISO 179/1eA |
36 |
Thermal properties
| Temperature of deflection under load |
1.80 MPa |
°C |
ISO 75-1,-2 |
102 |
| Temperature of deflection under load |
0.45 MPa |
°C |
ISO 75-1,-2 |
122 |
| Vicat softening temperature |
50 N; 50 °C/h |
°C |
ISO 306 |
118 |
| Vicat softening temperature |
50 N; 120 °C/h |
°C |
ISO 306 |
120 |
| Coefficient of linear thermal expansion, parallel |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
0.8 |
| Coefficient of linear thermal expansion, normal |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
0.85 |
| Burning behavior UL 94 [UL recognition] |
0.85 mm |
Class |
UL 94 |
HB |
| Oxygen index |
Method A |
% |
ISO 4589-2 |
24 |
Electrical properties (23 °C/50 % r. h.)
| Relative permittivity |
100 Hz |
– |
IEC 60250 |
3.1 |
| Relative permittivity |
1 MHz |
– |
IEC 60250 |
3.0 |
| Dissipation factor |
100 Hz |
10-4 |
IEC 60250 |
30 |
| Dissipation factor |
1 MHz |
10-4 |
IEC 60250 |
85 |
| Volume resistivity |
|
Ohm·m |
IEC 60093 |
1E14 |
| Surface resistivity |
|
Ohm |
IEC 60093 |
1E16 |
| Electrical strength |
1 mm |
kV/mm |
IEC 60243-1 |
35 |
| Comparative tracking index CTI |
Solution A |
Rating |
IEC 60112 |
250 |
Other properties (23 °C)
| Water absorption (saturation value) |
Water at 23 °C |
% |
ISO 62 |
0.7 |
| Water absorption (equilibrium value) |
23 °C; 50 % r. h. |
% |
ISO 62 |
0.2 |
| Density |
|
kg/m³ |
ISO 1183-1 |
1130 |
Processing conditions for test specimens
| Injection molding – Melt temperature |
|
°C |
ISO 294 |
260 |
| Injection molding – Mold temperature |
|
°C |
ISO 294 |
80 |
| Injection molding – Injection velocity |
|
mm/s |
ISO 294 |
240 |