ABS-CHIMEI-PA-717C
| Physical Properties | Metric | English | Comments |
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 – 0.0070 cm/cm | 0.0030 – 0.0070 in/in | ASTM D955 |
|
Melt Flow |
1.8 g/10 min
@Load 5.00 kg, Temperature 200 °C |
1.8 g/10 min
@Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 12 g/10 min
@Load 10.0 kg, Temperature 220 °C |
12 g/10 min
@Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Ball Indentation Hardness | 97.0 MPa | 14100 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 69.0 MPa | 10000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
|
Izod Impact, Notched |
2.55 J/cm
@Thickness 6.35 mm |
4.78 ft-lb/in
@Thickness 0.250 in |
ASTM D256 |
| 2.88 J/cm
@Thickness 3.17 mm |
5.40 ft-lb/in
@Thickness 0.125 in |
ASTM D256 |
|
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
Specification: ABS-CHIMEI-PA-717C
|