Product Description
A hard, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream.
| Physical |
Typical Value (English) Typical Value |
(SI) Test Based On |
| Specific Gravity |
0.960 0.960 |
ASTM D792 |
| Density |
0.960 g/cm³ 0.960 |
g/cm³ ISO 1183 |
| Outdoor Suitability |
f1 f1 |
UL 746C |
| Detergent Resistance |
f3 f3 |
UL 749 |
| Detergent Resistance |
f4 f4 |
UL 2157 |
|
|
|
| Hardness |
Typical Value (English) Typical Value |
(SI) Test Based On |
| Shore Hardness |
|
ISO 868 |
| Shore A, 15 sec, 73°F (23°C) |
93 93 |
|
| Elastomers |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Tensile Stress at 100% – Across Flow (73°F (23°C)) |
1030 |
psi |
7.10 |
MPa |
ASTM D412 |
| Tensile Stress at 100% – Across Flow (73°F (23°C)) |
1030 |
psi |
7.10 |
MPa |
ISO 37 |
| Tensile Strength at Break – Across Flow (73°F (23°C)) |
2180 |
psi |
15.0 |
MPa |
ASTM D412 |
| Tensile Stress at Break – Across Flow (73°F (23°C)) |
2180 |
psi |
15.0 |
MPa |
ISO 37 |
| Elongation at Break – Across Flow (73°F (23°C)) |
580 |
% |
580 |
% |
ASTM D412 |
| Tensile Strain at Break – Across Flow (73°F (23°C)) |
580 |
% |
580 |
% |
ISO 37 |
| Tear Strength – Across Flow (73°F (23°C), Die C) |
297 |
lbf/in |
52.0 |
kN/m |
ASTM D624 |
| Tear Strength – Across Flow |
|
|
|
|
ISO 34-1 |
| 73°F (23°C), Method Bb, Angle (Nicked) |
300 |
lbf/in |
52 |
kN/m |
|
| Compression Set |
|
|
|
|
ASTM D395B |
| 158°F (70°C), 22 hr, Type 1 |
36 |
% |
36 |
% |
|
| 257°F (125°C), 70 hr, Type 1 |
44 |
% |
44 |
% |
|
| Compression Set |
|
|
|
|
ISO 815 |
| 158°F (70°C), 22 hr, Type A |
36 |
% |
36 |
% |
|
| 257°F (125°C), 70 hr, Type A |
44 |
% |
44 |
% |
|
|
|
|
|
|
|
| Thermal |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Brittleness Temperature |
-65 |
°F |
-54 |
°C |
ASTM D746 |
| Brittleness Temperature |
-65 |
°F |
-54 |
°C |
ISO 812 |
| RTI Elec |
194 |
°F |
90.0 |
°C |
UL 746 |
| RTI Str |
|
|
|
|
UL 746 |
| 0.04 in (1.0 mm) |
194 |
°F |
90.0 |
°C |
|
| 0.06 in (1.5 mm) |
194 |
°F |
90.0 |
°C |
|
| 0.12 in (3.0 mm) |
203 |
°F |
95.0 |
°C |
|
|
|
|
|
|
|
| Electrical |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Dielectric Strength |
|
|
|
|
ASTM D149 |
| 73°F (23°C), 0.0787 in (2.00 mm) |
750 |
V/mil |
30 |
kV/mm |
|
| Dielectric Constant |
|
|
|
|
ASTM D150 |
| 73°F (23°C), 0.0780 in (1.98 mm) |
2.60 |
|
2.60 |
|
|
| Dielectric Constant |
|
|
|
|
IEC 60250 |
| 73°F (23°C), 0.0780 in (1.98 mm) |
2.60 |
|
2.60 |
|
|
| Comparative Tracking Index (CTI) |
PLC 0 |
|
PLC 0 |
|
UL 746 |
| High Amp Arc Ignition (HAI) |
PLC 0 |
|
PLC 0 |
|
UL 746 |
| High Voltage Arc Resistance to Ignition (HVAR) |
PLC 5 |
|
PLC 5 |
|
UL 746 |
| High Voltage Arc Tracking Rate (HVTR) |
PLC 1 |
|
PLC 1 |
|
UL 746 |
| Hot-wire Ignition (HWI) |
|
|
|
|
UL 746 |
| 0.04 in (1.0 mm) |
PLC 4 |
|
PLC 4 |
|
|
| 0.06 in (1.5 mm) |
PLC 3 |
|
PLC 3 |
|
|
| 0.12 in (3.0 mm) |
PLC 2 |
|
PLC 2 |
|
|