| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.920 | g/cm³ | 0.920 | g/cm³ | ASTM D792 |
| Base Density | 0.920 | g/cm³ | 0.920 | g/cm³ | Dow Method 1 |
| Melt Index (190°C/2.16 kg) | 1.0 | g/10 min | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 1.0 | mil | 25 | µm | |
| Film Puncture Energy | 315 | in·lb | 35.6 | J | Dow Method |
| Film Puncture Force | 47.0 | lbf | 209 | N | Dow Method |
| Film Puncture Resistance | 14.0 | ft·lb/in³ | 1.16 | J/cm³ | Dow Method |
| Film Toughness
MD |
1430 |
ft·lb/in³ |
118 |
J/cm³ |
ASTM D882 |
| TD | 1560 | ft·lb/in³ | 129 | J/cm³ | |
| Secant Modulus
1% Secant, MD |
34400 |
psi |
237 |
MPa |
ASTM D882 |
| 2% Secant, MD | 29800 | psi | 205 | MPa | |
| 1% Secant, TD | 39900 | psi | 275 | MPa | |
| 2% Secant, TD | 33600 | psi | 232 | MPa | |
| Tensile Strength
MD: Yield |
1650 |
psi |
11.3 |
MPa |
ASTM D882 |
| TD: Yield | 1730 | psi | 11.9 | MPa | |
| MD: Break | 6870 | psi | 47.4 | MPa | |
| TD: Break | 5890 | psi | 40.6 | MPa | |
| Tensile Elongation
MD: Break |
600 |
% |
600 |
% |
ASTM D882 |
| TD: Break | 740 | % | 740 | % | |
| Dart Drop Impact | 220 | g | 220 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD |
370 |
g |
370 |
g |
ASTM D1922 2 |
| TD | 630 | g | 630 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 223 | °F | 106 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 246 | °F | 119 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss | 60 | 60 | ASTM D2457 | ||
| Haze | 10 | % | 10 | % | ASTM D1003 |