Product Description
High Heat Resistance,High Flow, Glass fiber reinforced, Standard
Physical | Nominal Value Unit | Test Method |
Density | 1.61 g/cm³ | ISO 1183 |
Molding Shrinkage 4
Across Flow : 1.00 mm |
0.54 % |
Internal Method |
Flow : 1.00 mm | 0.020 % | |
Water Absorption (23°C, 24 hr) | 0.030 % | ISO 62 |
Mechanical | Nominal Value Unit | Test Method |
Tensile Strength | 175 MPa | ASTM D638 |
Tensile Elongation (Break) | 2.0 % | ASTM D638 |
Flexural Modulus | 15000 MPa | ISO 178 |
Flexural Stress | 220 MPa | ISO 178 |
Flexural Strain | 2.3 % | ISO 178 |
Impact | Nominal Value Unit | Test Method |
Charpy Notched Impact Strength | 35 kJ/m² | ISO 179/1eA |
Hardness | Nominal Value Unit | Test Method |
Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
Thermal | Nominal Value Unit | Test Method |
Heat Deflection Temperature
0.45 MPa, Unannealed |
290 °C |
ISO 75-2/B |
1.8 MPa, Unannealed | 280 °C | ISO 75-2/A |
Electrical | Nominal Value Unit | Test Method |
Volume Resistivity | 9.0E+15 ohms·cm | IEC 60093 |
Electric Strength
1.00 mm |
44 kV/mm |
IEC 60243-1 |
3.00 mm | 24 kV/mm | |
Dielectric Constant
1 kHz |
4.30 |
IEC 60250 |
1 MHz | 3.80 | |
Dissipation Factor
1 kHz |
0.020 |
IEC 60250 |
1 MHz | 0.030 | |
Arc Resistance | 130 sec | |
Comparative Tracking Index | 125 V | IEC 60112 |
Flammability | Nominal Value Unit | Test Method |
Flame Rating | V-0 | UL 94 |
Specification: LCP-Polyplastic-LAPEROS E130i
|