DESCRIPTION

RG568MO is a transparent polypropylene random ethylene copolymer based on proprietary Borstar Nucleation Technology (BNT) with high melt flow. This clarified product is designed for high speed injection moulding at low temperature and contains antistatic additives.

Articles produced from this product have excellent transparency, good impact strength at ambient temperatures, good organoleptic, good colour aesthetics and demoulding properties without plate-out or blooming issues.

PHYSICAL PROPERTIES

Density	900-910kg/m³	ISO 1183
Melt Flow Rate (230°C/2.16kg)	30g/10min	ISO 1133
Tensile Modulus (1mm/min)	1100MPa	ISO 527-2
Tensile Strain at Yield (50mm/min)	12%	ISO 527-2
Tensile Stress at Yield (50mm/min)	28MPa	ISO 527-2
Flexural Modulus	1150MPa	ISO 178
Flexural Modulus(by 1% secant)	1100MPa	ASTM D790A
Charpy Impact Strength, notched (23°C)	6kJ/m²	ISO 179/1eA
IZOD Impact Strength, notched (23°C)	50J/m	ASTM D256
Heat Deflection Temperature(0,45MPa)**	75°C	ISO 75-2
Vicat Softening Temperature(Method A)***	124,5°C	ISO 306
Haze(2mm)	20%	ASTM D1003
Hardness, Rockwell(R-scale)	92	ISO 2039-2

Specification: PPR MOULDING-BOROUGE-RG568MO

ALPHA	B
Group	PP RANDOM
Class	PPR MOULDING
GRADE	RG568MO
MFI	30
PROCESS	MOULDING
Country	Austria
Tds-Name	BOROUGE_RG568MO.pdf