ABS MOULDING-LG-XR404

Add to compare
Sold by
@ Plastic Dealer

Report Abuse
ABS MOULDING-LG-XR404
SKU: ABS MOULDING-LG-XR404 Categories: , Tags: , , , , ,
Physical Properties Original Value Comments
Specific Gravity 1.05 g/cc ASTM D792
Maximum Moisture Content 0.010 Injection Molding
Linear Mold Shrinkage, Flow 0.0040 – 0.0070 cm/cm
@Thickness 3.20 mm
ASTM D955
Melt Flow 7.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C
ASTM D1238
Mechanical Properties Original Value Comments
Hardness, Rockwell R 108 ASTM D785
Tensile Strength, Yield 490 kg(f)/cm²
@Thickness 3.20 mm
50 mm/min; ASTM D638
Elongation at Break 25 %
@Thickness 3.20 mm
50 mm/min; ASTM D638
Flexural Yield Strength 790 kg(f)/cm²
@Thickness 3.20 mm
15 mm/min; ASTM D790
Flexural Modulus 26000 kg(f)/cm²
@Thickness 3.20 mm
15 mm/min; ASTM D790
Izod Impact, Notched 20.0 kg-cm/cm
@Thickness 6.40 mm,
Temperature 23.0 °C
ASTM D256
22.0 kg-cm/cm
@Thickness 3.20 mm,
Temperature 23.0 °C
ASTM D256
Izod Impact, Unnotched 6.00 kg-cm/cm
@Thickness 6.40 mm,
Temperature -30.0 °C
ASTM D256
7.00 kg-cm/cm
@Thickness 3.20 mm,
Temperature -30.0 °C
ASTM D256
Electrical Properties Original Value Comments
Volume Resistivity 1.00e+15 ohm-cm ASTM D257
Dielectric Strength 33.0 kV/mm
@Thickness 1.00 mm
ASTM D149
Arc Resistance 60 – 120 sec ASTM D495
Comparative Tracking Index >= 600 V Solution A; IEC 60112
Hot Wire Ignition, HWI 7.0 – 15 sec
@Thickness >=1.50 mm
15 – 30 sec
@Thickness >=3.00 mm
High Amp Arc Ignition, HAI 60 – 120 arcs
@Thickness 1.50 mm
>= 120 arcs
@Thickness 3.00 mm
High Voltage Arc-Tracking Rate, HVTR 25.4 – 50.0 mm/min
Thermal Properties Original Value Comments
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
@Thickness 6.40 mm
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
@Thickness 6.40 mm
Unannealed; ASTM D648
Vicat Softening Point 108 °C
@Load 5.00 kg
50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C
@Thickness >=1.50 mm
UL 746B
60.0 °C
@Thickness >=3.00 mm
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
@Thickness >=1.50 mm
UL 746B
60.0 °C
@Thickness >=3.00 mm
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
@Thickness >=1.50 mm
UL 746B
60.0 °C
@Thickness >=3.00 mm
UL 746B
Flammability, UL94 HB
@Thickness >=1.50 mm
HB
@Thickness >=3.00 mm
Processing Properties Original Value Comments
Rear Barrel Temperature 180 – 210 °C Injection Molding
Middle Barrel Temperature 210 – 230 °C Injection Molding
Front Barrel Temperature 230 – 240 °C Injection Molding
Nozzle Temperature 230 – 240 °C Injection Molding
Melt Temperature 220 – 240 °C Injection Molding
Mold Temperature 40.0 – 60.0 °C Injection Molding
Drying Temperature 80.0 – 90.0 °C Injection Molding
Dry Time 3.00 – 4.00 hour Injection Molding
Back Pressure 29.4 – 58.8 MPa Injection Molding
Screw Speed 50 – 100 rpm Injection Molding

Specification: ABS MOULDING-LG-XR404

ALPHA

L

Group

ABS

Class

ABS MOULDING

GRADE

XR404

MFI

7

PROCESS

MOULDING

Country

South Korean

Tds-Name

LG_ABS_XR_404_(NATURAL).pdf

Tds-Url

https://www.matweb.com/search/datasheet.aspx?matguid=7b4e26946cf147d2b0ef935a6af41136&n=1

D-Type

S

Brand

L>LG

User Reviews

0.0 out of 5
0
0
0
0
0
Write a review

There are no reviews yet.

Be the first to review “ABS MOULDING-LG-XR404”

Your email address will not be published. Required fields are marked *

Vendor Information

  • No ratings found yet!
Add to compare
ASA+PC-SABIC-GELOY HRA170
Add to compare
ASA+PC-CHIMEI-ABS PC-365
Add to compare
LL FILM-SABIC-218NJ
Add to compare
LD FILM-SABIC-HP0823JN
Add to compare
BOPP-LUBAN-HP3107K

Product Enquiry

Plastic Dealers
Logo
Reset Password
Compare items
  • Total (0)
Compare
0
Shopping cart