Lotrène® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer.
They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
Lotrène® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks,
refuse, tunnel films, mulching films…
| Physical | Nominal Value Unit | Test Method |
| Specific Gravity | 0.918 g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 g/10 min | ASTM D1238 |
| Films | Nominal Value Unit | Test Method |
| Secant Modulus
1% Secant, MD: 40 µm, Blown Film |
215 MPa |
ASTM D882 |
| 1% Secant, TD: 40 µm, Blown Film | 245 MPa | |
| Tensile Strength
MD: Yield, 40 µm, Blown Film |
11.0 MPa |
ASTM D882 |
| TD: Yield, 40 µm, Blown Film MD: Break, 40 µm, Blown Film
TD: Break, 40 µm, Blown Film |
11.0 MPa
38.0 MPa 33.0 MPa |
|
| Tensile Elongation
MD: Break, 40 µm, Blown Film |
800 % |
ASTM D882 |
| TD: Break, 40 µm, Blown Film | 850 % | |
| Dart Drop Impact 2 (40 µm, Blown Film) | 150 g | ASTM D1709 |
| Elmendorf Tear Strength
MD: 40 µm, Blown Film |
280 g |
ASTM D1922 |
| TD: 40 µm, Blown Film | 480 g | |
| Thermal | Nominal Value Unit | Test Method |
| Vicat Softening Temperature | 100 °C | ASTM D1525 |
| Peak Crystallization Temperature (DSC) | 122 °C | Internal Method |
| Optical | Nominal Value Unit | Test Method |
| Gloss (45°, 40.0 µm, Blown Film) | 60 | ASTM D2457 |
| Haze (40.0 µm, Blown Film) | 11 % | ASTM D1003 |