| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 100 MPa | 14500 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 120 % | 120 % | 50 mm/min; ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | ISO 180/4A |
| Charpy Impact, Notched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | annealed; ISO 75 |
| 143 °C | 289 °F | unannealed; ISO 75 | |
Vicat Softening Point  |
145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 150 °C @Load 1.00 kg |
302 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
|
Specification: PC-CHIMEI-110V
|