Product Description
An impact copolymer resin designed for consumer and industrial products requiring very high impact resistance.
| General | |||
| Availability 1 | • Asia Pacific | ||
| Features | • Balanced Stiffness/Toughness
• High Stiffness |
• Medium Flow
• Ultra High Impact Resistance |
|
| Uses | • Appliance Components
• Battery Cases |
• Consumer Applications
• Industrial Applications |
• Rigid Packaging
• Toys |
| Appearance | • Natural Color | ||
| Form(s) | • Pellets | ||
| Processing Method | • Injection Molding | ||
| Revision Date | • 08/01/2015 | ||
| Physical | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | 4.0 | g/10 min | ASTM D1238 |
| Density | 0.900 | g/cm³ | 0.900 | g/cm³ | ExxonMobil Method |
| Mechanical | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Tensile Strength at Yield | ASTM D638 | ||||
| 2.0 in/min (51 mm/min) | 3440 | psi | 23.7 | MPa | |
| Tensile Stress at Yield | 3340 | psi | 23.0 | MPa | ISO 527-2/50 |
| Elongation at Yield (2.0 in/min (51 mm/min)) | 6.0 | % | 6.0 | % | ASTM D638 |
| Tensile Strain at Yield | 5.6 | % | 5.6 | % | ISO 527-2/50 |
| Tensile Modulus | 173000 | psi | 1200 | MPa | ISO 527-2/1 |
| Flexural Modulus – 1% Secant | |||||
| 0.051 in/min (1.3 mm/min) | 176000 | psi | 1210 | MPa | ASTM D790A |
| 0.51 in/min (13 mm/min) | 188000 | psi | 1300 | MPa | ASTM D790B |
| Flexural Modulus
(0.079 in/min (2.0 mm/min)) |
165000 | psi | 1140 | MPa | ISO 178 |
| Impact | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Notched Izod Impact (73°F (23°C)) | No Break | No Break | ASTM D256A | ||
| Notched Izod Impact Strength | ISO 180/1A | ||||
| -40°F (-40°C) | 4.3 | ft·lb/in² | 9.0 | kJ/m² | |
| 0°F (-18°C) | 5.2 | ft·lb/in² | 11 | kJ/m² | |
| 73°F (23°C) | 25 | ft·lb/in² | 53 | kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | ||||
| -22°F (-30°C) | 3.2 | ft·lb/in² | 6.8 | kJ/m² | |
| 73°F (23°C) | 27 | ft·lb/in² | 57 | kJ/m² | |
| Thermal | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Heat Deflection Temperature (1.80 MPa) | 122 | °F | 50.2 | °C | ISO 75-2/A |
| Heat Deflection Temperature (0.45 MPa) | 180 | °F | 82.0 | °C | ISO 75-2/Bf |
| Deflection Temperature Under Load (DTUL) at 66psi – Unannealed | 195 | °F | 90.6 | °C | ASTM D648 |
| DTUL @ 66psi – Annealed | 234 | °F | 112 | °C | ASTM D648 |
| Hardness | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Rockwell Hardness | 84 | 84 | ASTM D785 |
Specification: PP-CP-ExxonMobil-7032E3′
|