PC-CHIMEI-122
| Properties | ISO Test Method | Test Condition | Unit | General | |
| Melt Flow Index | 1133 | 300 × 1.2KG | ml/10 min | 22 | |
| Melt Flow Index | 1133 | 300 × 1.2KG | ml/10 min | 22 | |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 63 | |
| 50 mm/min, break | MPa | 70 | |||
| Tensile Elongation | 527 | 50 mm/min | % | 120 | |
| Flexural Strength | 178 | 2 mm/min | MPa | 90 | |
| 2 mm/min | GPa | 2.4 | |||
| Izod Impact Strength | 180/4A | 23 Notched | KJ/m2 | 60 | |
| Charpy Impact Strength |
|
23 Notched | KJ/m2 | 60 | |
| Vicat Softening Temp. | 306 | 1 Kg,50 | /hr | 150 | |
| 5 Kg,50 | /hr | 145 | |||
| Heat Distortion Temp | 75/A | 1.8 MPa | Unannealed | 128 | |
| 1.8 MPa | Annealed | 143 | |||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 6.0~8.0×10-5 | |
| Flammability | – | UL-94 | – | 3.0mm V-2 | |
| Mold Shrinkage | 294-4 | – | % | 0.5~0.7 | |
| Symbol | 1043 | – | – | >PC< |
Specification: PC-CHIMEI-122
|