Product Description
Amilan® CM1001G-20 is a Polyamide 6 (Nylon 6) product filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated.
| Physical |
Dry |
Conditioned |
Unit |
Test Method |
| Density |
1.29 |
— |
g/cm³ |
ISO 1183 |
| Molding Shrinkage |
|
|
|
Internal Method |
| Across Flow : 3.00 mm |
0.60 to 0.90 |
— |
% |
|
| Flow : 3.00 mm |
0.30 to 0.50 |
— |
% |
|
| Water Absorption |
|
|
|
ISO 62 |
| 23°C, 24 hr |
1.3 |
— |
% |
|
| Saturation, 23°C |
7.8 |
— |
% |
|
| Mechanical |
Dry |
Conditioned |
Unit |
Test Method |
| Tensile Stress (Yield, 23°C) |
120 |
— |
MPa |
ISO 527-2 |
| Tensile Strain |
|
|
|
ISO 527-2 |
| Break, -40°C |
2.5 |
3.0 |
% |
|
| Break, 23°C |
3.0 |
4.5 |
% |
|
| Break, 80°C |
5.0 |
5.5 |
% |
|
| Flexural Modulus |
|
|
|
ISO 178 |
| -40°C |
8700 |
7300 |
MPa |
|
| 23°C |
6800 |
3500 |
MPa |
|
| 80°C |
3200 |
2600 |
MPa |
|
| Flexural Stress |
|
|
|
ISO 178 |
| -40°C |
275 |
— |
MPa |
|
| 23°C |
205 |
— |
MPa |
|
| 80°C |
115 |
— |
MPa |
|
| Compressive Stress |
|
|
|
ISO 604 |
| -40°C |
240 |
— |
MPa |
|
| 23°C |
155 |
80.0 |
MPa |
|
| 80°C |
90.0 |
— |
MPa |
|
| Shear Strength (23°C) |
115 |
65.0 |
MPa |
ASTM D732 |
| Coefficient of Friction |
|
|
|
|
| — 4 |
< 0.15 |
— |
|
|
| — 5 |
0.30 |
— |
|
|
| Taber Abrasion Resistance (1000 Cycles) |
12.0 |
— |
mg |
|
| Impact |
Dry |
Conditioned |
Unit |
Test Method |
| Charpy Notched Impact Strength |
|
|
|
ISO 179 |
| -40°C |
6.0 |
7.0 |
kJ/m² |
|
| 23°C |
7.0 |
8.5 |
kJ/m² |
|
There are no reviews yet.