ABS-CHIMEI-PA-737
Product Description
POLYLAC® PA-737 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.
| Physical
Specific Gravity — |
Nominal Value (English)
1.04 |
Nominal Value (SI)
1.04 g/cm³ |
Test Method
ASTM D792 |
| 73°F (23°C) | 1.04 g/cm³ | 1.04 g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR)
200°C/5.0 kg |
2.6 g/10 min |
2.6 g/10 min |
ASTM D1238 |
| 220°C/10.0 kg | 33 g/10 min | 33 g/10 min | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 2.01 in³/10min | 33.0 cm³/10min | ISO 1133 |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Tensile Stress
Yield |
5510 psi |
38.0 MPa |
ISO 527-2/50 |
| Break | 4640 psi | 32.0 MPa | ISO 527-2/50 |
| 0.118 in (3.00 mm) 4 | 5120 psi | 35.3 MPa | ASTM D638 |
| Tensile Elongation
Break, 0.118 in (3.00 mm) 4 |
22 % |
22 % |
ASTM D638 |
| Break | 20 % | 20 % | ISO 527-2/50 |
| Flexural Modulus
0.236 in (6.00 mm) 5 |
284000 psi |
1960 MPa |
ASTM D790 |
| — 6 | 276000 psi | 1900 MPa | ISO 178 |
| Flexural Strength
0.236 in (6.00 mm) 5 |
8390 psi |
57.9 MPa |
ASTM D790 |
| — 6 | 8700 psi | 60.0 MPa | ISO 178 |
| Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Charpy Notched Impact Strength | 10 ft·lb/in² | 21 kJ/m² | ISO 179 |
| Notched Izod Impact
73°F (23°C), 0.118 in (3.00 mm) |
4.6 ft·lb/in |
250 J/m |
ASTM D256 |
| 73°F (23°C), 0.236 in (6.00 mm) | 3.3 ft·lb/in | 180 J/m | ASTM D256 |
| — | 9.0 ft·lb/in² | 19 kJ/m² | ISO 180/1A |
| Hardness | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Rockwell Hardness (R-Scale) | 103 | 103 | ASTM D785 |
| Ball Indentation Hardness (H 358/30) | 13600 psi | 94.0 MPa | ISO 2039-1 |