LL METALLOCENE-ExxonMobil-3518PA
@ Plastic Dealer Ask owner
Product Description
Exceed 3518PA resin is an ethylene 1-hexene copolymer. Films made from Exceed 3518PA resin have outstanding tensile properties and impact and puncture toughness. These superior properties, along with excellent drawability, make these resins versatile for both monolayer and multilayer cast packaging film. TnPP is not intentionally added to Exceed 3518PA.
| Resin Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Density | 0.918 | g/cm³ | 0.918 | g/cm³ | ASTM D1505 |
| Melt Index (190°C/2.16 kg) | 3.5 | g/10 min | 3.5 | g/10 min | ASTM D1238 |
| Peak Melting Temperature | 237 | °F | 114 | °C | ExxonMobil Method |
| Film Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Tensile Strength at Yield MD | 1200 | psi | 8.3 | MPa | ASTM D882 |
| Tensile Strength at Yield TD | 1100 | psi | 7.6 | MPa | ASTM D882 |
| Tensile Strength at Break MD | 11000 | psi | 70 | MPa | ASTM D882 |
| Tensile Strength at Break TD | 6800 | psi | 47 | MPa | ASTM D882 |
| Elongation at Break MD | 510 | % | 510 | % | ASTM D882 |
| Elongation at Break TD | 680 | % | 680 | % | ASTM D882 |
| Secant Modulus MD – 1% Secant | 16000 | psi | 110 | MPa | ASTM D882 |
| Secant Modulus TD – 1% Secant | 18000 | psi | 120 | MPa | ASTM D882 |
| Dart Drop Impact | 140 | g | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength MD | 190 | g | 190 | g | ASTM D1922 |
| Elmendorf Tear Strength TD | 500 | g | 500 | g | ASTM D1922 |
| Puncture Force | 11 | lbf | 47 | N | ExxonMobil Method |
| Puncture Energy | 38 | in·lb | 4.3 | J | ExxonMobil Method |
| Optical Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Gloss (60°) | 86 | 86 | ASTM D2457 | ||
| Haze | 2.4 | % | 2.4 | % | ASTM D1003 |
Specification: LL METALLOCENE-ExxonMobil-3518PA
|