| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.915 | g/cm³ | 0.915 | g/cm³ | ASTM D792 |
| Melt Index (190°C/2.16 kg) | 3.5 | g/10 min | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 1 | mil | 20 | µm | |
| Film Puncture Energy (0.80 mil (20 µm)) | 36.0 | in·lb | 4.07 | J | Dow Method |
| Film Puncture Force
0.80 mil (20 µm) |
10.0 |
lbf |
44.5 |
N |
Dow Method |
| 0.80 mil (20 µm) 1 | 11.0 | lbf | 48.9 | N | |
| Film Puncture Resistance (0.80 mil (20 µm)) | 323 | ft·lb/in³ | 26.7 | J/cm³ | Dow Method |
| Tensile Strength
MD : Yield, 0.80 mil (20 µm) |
1300 |
psi |
8.96 |
MPa |
ASTM D882 |
| TD : Yield, 0.80 mil (20 µm) | 1220 | psi | 8.41 | MPa | |
| MD : Break, 0.80 mil (20 µm) | 5800 | psi | 40.0 | MPa | |
| TD : Break, 0.80 mil (20 µm) | 5200 | psi | 35.9 | MPa | |
| Tensile Elongation
MD : Break, 0.80 mil (20 µm) |
450 |
% |
450 |
% |
ASTM D882 |
| TD : Break, 0.80 mil (20 µm) | 650 | % | 650 | % | |
| Dart Drop Impact (0.80 mil (20 µm)) | 630 | g | 630 | g | ASTM D1709B |
| Elmendorf Tear Strength
MD : 0.80 mil (20 µm) |
390 |
g |
390 |
g |
ASTM D1922 |
| TD : 0.80 mil (20 µm) | 600 | g | 600 | g | |
| Ultimate Stretch 2 (0.8 mil (20.3 µm)) | 300 | % | 300 | % | Dow Method |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 210 | °F | 98.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 253 | °F | 123 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (45°, 0.800 mil (20.3 µm)) | 96 | 96 | ASTM D2457 | ||
| Haze (0.800 mil (20.3 µm)) | 0.600 | % | 0.600 | % | ASTM D1003 |
| Extrusion | Nominal Value | (English) | Nominal Value | (SI) | |
| Melt Temperature | 520 | °F | 271 | °C | |
Specification: LL FILM-DOW-5220G
|