LL METALLOCENE-ExxonMobil-2012MK
@ Plastic Dealer Ask owner
Product Description
Exceed™ 2012 Series are ethylene 1-hexene copolymer resins. Films made from these resins have outstanding toughness, impact strength and puncture. These superior strength properties, along with excellent heat sealing and hot tack performance, make this a very versatile packaging film resin. TnPP is not intentionally added to Exceed™ 2012 resin.
| Resin Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Density / Specific Gravity | 0.912 | g/cm³ | 0.912 | g/cm³ | ASTM D792 |
| Melt Index (190°C/2.16 kg) | 2.0 | g/10 min | 2.0 | g/10 min | ASTM D1238 |
| Peak Melting Temperature | 237 | °F | 114 | °C | ExxonMobil Method |
| Thermal | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Vicat Softening Temperature | 205 | °F | 96.0 | °C | ExxonMobil Method |
| Film Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Tensile Strength at Yield MD | 910 | psi | 6.3 | MPa | ASTM D882 |
| Tensile Strength at Yield TD | 860 | psi | 6.0 | MPa | ASTM D882 |
| Tensile Strength at Break MD | 10000 | psi | 70 | MPa | ASTM D882 |
| Tensile Strength at Break TD | 8200 | psi | 60 | MPa | ASTM D882 |
| Elongation at Break MD | 560 | % | 560 | % | ASTM D882 |
| Elongation at Break TD | 610 | % | 610 | % | ASTM D882 |
| Secant Modulus MD – 1% Secant | 15000 | psi | 100 | MPa | ASTM D882 |
| Secant Modulus TD – 1% Secant | 15000 | psi | 100 | MPa | ASTM D882 |
| Dart Drop Impact | 690 | g | 690 | g | ASTM D1709A |
| Elmendorf Tear Strength MD | 240 | g | 240 | g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 | g | 300 | g | ASTM D1922 |
| Puncture Force | 13 | lbf | 57 | N | ExxonMobil Method |
| Puncture Energy | 47 | in·lb | 5.3 | J | ExxonMobil Method |
| Optical Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Gloss (45°) | 33 | 33 | ASTM D2457 | ||
| Haze | 21 | % | 21 | % | ASTM D1003 |
Specification: LL METALLOCENE-ExxonMobil-2012MK
|