Product Description
Enable™ 2703MC resin is an ethylene 1-hexene copolymer. Enable™ performance polymer resins offer an outstanding balance between processing and film properties, including tensile, impact and puncture. Easier processing and excellent properties lead to significant high pressure LDPE replacement in many applications, yet with superior drawdown and enhanced toughness. TnPP is not intentionally added to Enable™ 2703MC resin.
| Resin Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Density |
0.927 |
g/cm³ |
0.927 |
g/cm³ |
ASTM D1505 |
| Melt Index (190°C/2.16 kg) |
0.30 |
g/10 min |
0.30 |
g/10 min |
ASTM D1238 |
| Peak Melting Temperature |
246 |
°F |
119 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Thermal |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Vicat Softening Temperature |
239 |
°F |
115 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Film Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Tensile Strength at Yield MD |
1900 |
psi |
13 |
MPa |
ASTM D882 |
| Tensile Strength at Yield TD |
2200 |
psi |
15 |
MPa |
ASTM D882 |
| Tensile Strength at Break MD |
9100 |
psi |
60 |
MPa |
ASTM D882 |
| Tensile Strength at Break TD |
7500 |
psi |
50 |
MPa |
ASTM D882 |
| Elongation at Break MD |
480 |
% |
480 |
% |
ASTM D882 |
| Elongation at Break TD |
750 |
% |
750 |
% |
ASTM D882 |
| Secant Modulus MD – 1% Secant |
45000 |
psi |
310 |
MPa |
ASTM D882 |
| Secant Modulus TD – 1% Secant |
55000 |
psi |
380 |
MPa |
ASTM D882 |
| Dart Drop Impact |
140 |
g |
140 |
g |
ASTM D1709A |
| Elmendorf Tear Strength MD |
40 |
g |
40 |
g |
ASTM D1922 |
| Elmendorf Tear Strength TD |
670 |
g |
670 |
g |
ASTM D1922 |
| Puncture Force |
11 |
lbf |
50 |
N |
ExxonMobil Method |
| Puncture Energy |
25 |
in·lb |
2.8 |
J |
ExxonMobil Method |
| |
|
|
|
|
|
| Optical Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Gloss (45°) |
42 |
|
42 |
|
ASTM D2457 |
| Haze |
12 |
% |
12 |
% |
ASTM D1003 |