Product Description:
010F18S is a Linear Low Density Polyethylene manufactured using Nova Chemical’s Sclairtech Solution Polymerization Technology with following features:
- Good processability
- Good mechanical properties
- Contains slip & antiblock
Typical Properties:
| Tested Properties |
Test Method |
UOM |
Values* |
| Resin Properties |
| Melt Flow Index (1900C & 2.16 Kg) |
ASTM D 1238 |
gm/10 min |
0.90 |
| Density @ 23oC |
ASTM D 1505 |
gm/cm3 |
0.918 |
| Mechanical Properties |
| Tensile Strength @ Yield (50 mm/min) MD/TD |
ASTM D 882 |
MPa |
13/12 |
| Ultimate Tensile Strength (50 mm/min) MD/TD |
ASTM D 882 |
MPa |
39/30 |
| Elongation at Break(50 mm/min) MD/TD |
ASTM D 882 % |
700/850 |
| Dart Impact Strength (38mm dart,66cm height) |
ASTM D 1709 |
g/µ |
3.5 |
| Tear Strength |
ASTM D 1922 |
g/µ |
3.3/10.2 |
| Coefficient of Friction(Static/Dynamic) |
ASTM D 1894 |
0.22/0.16 |
| Gloss (600) |
ASTM D 523 % |
80 |
| Tested Properties |
Test Method |
UOM |
Values* |
| Resin Properties |
| Melt Flow Index (1900C & 2.16 Kg) |
ASTM D 1238 |
gm/10 min |
0.90 |
| Density @ 23oC |
ASTM D 1505 |
gm/cm3 |
0.918 |
| Mechanical Properties |
| Tensile Strength @ Yield (50 mm/min) MD/TD |
ASTM D 882 |
MPa |
13/12 |
| Ultimate Tensile Strength (50 mm/min) MD/TD |
ASTM D 882 |
MPa |
39/30 |
| Elongation at Break(50 mm/min) MD/TD |
ASTM D 882 % |
700/850 |
| Dart Impact Strength (38mm dart,66cm height) |
ASTM D 1709 |
g/µ |
3.5 |
| Tear Strength |
ASTM D 1922 |
g/µ |
3.3/10.2 |
| Coefficient of Friction(Static/Dynamic) |
ASTM D 1894 |
0.22/0.16 |
| Gloss (600) |
ASTM D 523 % |
80 |