Product Description
LL 1002AY is a butene LLDPE designed for the blown film process, offering high gloss and excellent draw down. Films made from LL1002AY have very good tensile and toughness properties. TnPP is not intentionally added to LL 1002AY.
| Resin Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Density |
0.918 |
g/cm³ |
0.918 |
g/cm³ |
ASTM D1505 |
| Melt Index (190°C/2.16 kg) |
2.0 |
g/10 min |
2.0 |
g/10 min |
ASTM D1238 |
| Peak Melting Temperature |
250 |
°F |
121 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Film Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Tensile Strength at Yield MD |
1400 |
psi |
9.4 |
MPa |
ASTM D882 |
| Tensile Strength at Yield TD |
1300 |
psi |
8.9 |
MPa |
ASTM D882 |
| Tensile Strength at Break MD |
7100 |
psi |
49 |
MPa |
ASTM D882 |
| Tensile Strength at Break TD |
4200 |
psi |
29 |
MPa |
ASTM D882 |
| Elongation at Break MD |
590 |
% |
590 |
% |
ASTM D882 |
| Elongation at Break TD |
800 |
% |
800 |
% |
ASTM D882 |
| Secant Modulus TD – 1% Secant |
32000 |
psi |
220 |
MPa |
ASTM D882 |
| Dart Drop Impact |
70 |
g |
70 |
g |
ASTM D1709A |
| Elmendorf Tear Strength MD |
90 |
g |
90 |
g |
ASTM D1922 |
| Elmendorf Tear Strength TD |
400 |
g |
400 |
g |
ASTM D1922 |
| |
|
|
|
|
|
| Optical Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Gloss (45°) |
76 |
|
76 |
|
ASTM D2457 |
| Haze |
4.4 |
% |
4.4 |
% |
ASTM D1003 |