| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.935 | g/cm³ | 0.935 | g/cm³ | ASTM D792 |
| Base Density 1 | 0.935 | g/cm³ | 0.935 | g/cm³ | Dow Method |
| Melt Index (190°C/2.16 kg) | 1.0 | g/10 min | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Puncture Resistance (1.0 mil (25 µm)) | 93.0 | ft·lb/in³ | 7.69 | J/cm³ | Dow Method |
| Film Toughness
MD : 1.0 mil (25 µm) |
1180 |
ft·lb/in³ |
97.5 |
J/cm³ |
ASTM D882 |
| TD : 1.0 mil (25 µm) | 1390 | ft·lb/in³ | 115 | J/cm³ | |
| Secant Modulus
2% Secant, MD : 1.0 mil (25 µm) |
54700 |
psi |
377 |
MPa |
ASTM D882 |
| 2% Secant, TD : 1.0 mil (25 µm) | 50500 | psi | 348 | MPa | |
| Tensile Strength
MD : Yield, 1.0 mil (25 µm) |
2210 |
psi |
15.2 |
MPa |
ASTM D882 |
| TD : Yield, 1.0 mil (25 µm) | 2430 | psi | 16.7 | MPa | |
| MD : Break, 1.0 mil (25 µm) | 5560 | psi | 38.3 | MPa | |
| TD : Break, 1.0 mil (25 µm) | 4810 | psi | 33.1 | MPa | |
| Tensile Elongation
MD : Break, 1.0 mil (25 µm) |
520 |
% |
520 |
% |
ASTM D882 |
| TD : Break, 1.0 mil (25 µm) | 660 | % | 660 | % | |
| Dart Drop Impact (1.0 mil (25 µm)) | 110 | g | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD : 1.0 mil (25 µm) |
71 |
g |
71 |
g |
ASTM D1922 |
| TD : 1.0 mil (25 µm) | 410 | g | 410 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 248 | °F | 120 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 259 | °F | 126 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (45°, 1.00 mil (25.4 µm)) | 58 | 58 | ASTM D2457 | ||
| Haze (1.00 mil (25.4 µm)) | 7.0 | % | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | (English) | Nominal Value | (SI) | |
| Melt Temperature | 400 to 475 | °F | 204 to 246 | °C | |
Specification: LL FILM-DOW-2038.68
|