LD LAMINATION-DOW-722
@ Plastic Dealer Ask owner
| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.918 | g/cm³ | 0.918 | g/cm³ | ASTM D792 |
| Base Density 1 | 0.918 | g/cm³ | 0.918 | g/cm³ | Dow Method |
| Melt Index (190°C/2.16 kg) | 8.0 | g/10 min | 8.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||||
| (ESCR) 2 | |||||
| 122°F (50°C), 100% Igepal, F50 | < 1.00 | hr | < 1.00 | hr | |
| Mechanical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Tensile Strength 2 | ASTM D638 | ||||
| Yield | 1200 | psi | 8.27 | MPa | |
| Break | 1400 | psi | 9.65 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||||
| Yield | 4.0 | % | 4.0 | % | |
| Break | 500 | % | 500 | % | |
| Flexural Modulus – 2% Secant 2 | 34000 | psi | 234 | MPa | ASTM D790B |
| Coefficient of Friction | 0.60 | 0.60 | ASTM D1894 | ||
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Seal Initiation Temperature 3 | 221 | °F | 105 | °C | Dow Method |
| Water Vapor Transmission Rate | 1.7 | g·mil/100in²/a tm/24 hr | 0.67 | g·mm/m²/atm ASTM F1249
/24 hr |
|
| Impact | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Tensile Impact Strength 4, 2 | 130 | ft·lb/in² | 273 | kJ/m² | ASTM D1822 |
| Hardness | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Durometer Hardness 2 (Shore D) | 43 | 43 | ASTM D2240 | ||
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Deflection Temperature Under Load 2 | ASTM D648 | ||||
| 66 psi (0.45 MPa), Unannealed | 99.0 | °F | 37.2 | °C | |
| Brittleness Temperature 2 | -76.0 | °F | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 190 | °F | 87.8 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 224 | °F | 107 | °C | Dow Method |
Specification: LD LAMINATION-DOW-722
|