Impact modified polyoxymethylene DuPont FG500P NC010 pom pellets Low friction plastic resin

Physical Properties

Metric

English

Comments

Density 

1.42 g/cc

0.0513 lb/in³

ISO 1183

Water Absorption 

1.4 %
@Thickness 2.00 mm

1.4 %
@Thickness 0.0787 in

Sim. to ISO 62

Moisture Absorption 

0.400 %
@Thickness 2.00 mm

0.400 %
@Thickness 0.0787 in

Sim. to ISO 62

Linear Mold Shrinkage, Flow 

0.020 cm/cm

0.020 in/in

ISO 294-4, 2577

Linear Mold Shrinkage, Transverse 

0.019 cm/cm

0.019 in/in

ISO 294-4, 2577

Melt Flow 

13 g/10 min
@Load 2.16 kg,
Temperature 190 °C

13 g/10 min
@Load 4.76 lb,
Temperature 374 °F

cm³/10min Volumetric; ISO 1133

15 g/10 min
@Load 2.16 kg,
Temperature 190 °C

15 g/10 min
@Load 4.76 lb,
Temperature 374 °F

ISO 1133

Mechanical Properties

Metric

English

Comments

Hardness, Rockwell M 

92

92

ISO 2039-2

Hardness, Rockwell R 

120

120

ISO 2039-2

Tensile Strength, Yield 

71.0 MPa

10300 psi

ISO 527-1/-2

Elongation at Break 

30 %

30 %

Nominal; ISO 527-1/-2

Elongation at Yield 

17 %

17 %

ISO 527-1/-2

Tensile Modulus 

3.10 GPa

450 ksi

ISO 527-1/-2

Flexural Strength 

80.0 MPa
@Strain 3.50 %

11600 psi
@Strain 3.50 %

ISO 178