high impact American DuPont POM 500T NC010 resin original plastic raw material pom pellest

Physical Properties

Metric

English

Comments

Density 

1.38 g/cc

0.0499 lb/in³

ISO 1183

Melt Density 

1.18 g/cc
@Temperature 205 °C

0.0426 lb/in³
@Temperature 401 °F

Water Absorption 

0.30 %
@Time 86400 sec

0.30 %
@Time 24.0 hour

Immersion; Sim. to ISO 62

0.82 %
@Thickness 2.00 mm

0.82 %
@Thickness 0.0787 in

Sim. to ISO 62

Moisture Absorption 

0.210 %
@Thickness 2.00 mm

0.210 %
@Thickness 0.0787 in

Sim. to ISO 62

Linear Mold Shrinkage, Flow 

0.015 cm/cm

0.015 in/in

ISO 294-4, 2577

Linear Mold Shrinkage, Transverse 

0.016 cm/cm

0.016 in/in

ISO 294-4, 2577

Melt Flow 

10 g/10 min@Load 2.16 kg,
Temperature 190 °C

10 g/10 min@Load 4.76 lb,
Temperature 374 °F

cm³/10min Volumetric; ISO 1133

12 g/10 min
@Load 2.16 kg,
Temperature 190 °C

12 g/10 min
@Load 4.76 lb,
Temperature 374 °F

ISO 1133

Mechanical Properties

Metric

English

Comments

Hardness, Rockwell M 

79

79

ISO 2039-2

Hardness, Rockwell R 

117

117

ISO 2039-2

Ball Indentation Hardness 

155 MPa

22500 psi

H 961/30; ISO 2039-1

Tensile Strength, Yield 

55.0 MPa

7980 psi

ISO 527-1/-2

Elongation at Break 

35 %

35 %

Nominal; ISO 527-1/-2