Covestro uv Makrolon 2400 Polycarbonate PC Plastic Granules PC Raw Material Resin

Physical Properties

Metric

English

Comments

Bulk Density 

0.660 g/cc

0.0238 lb/in³

pellets; ISO 60

Density 

1.20 g/cc

0.0434 lb/in³

ISO 1183-1

Moisture Absorption at Equilibrium 

0.12 %

0.12 %

ISO 62, 50% RH

Water Absorption at Saturation 

0.30 %

0.30 %

ISO 62

Water Vapor Transmission 

15.0 g/m²/day
@Thickness 0.100 mm

0.966 g/100 in²/day
@Thickness 0.00394 in

85% RH, film; ISO 15106-1

Oxygen Transmission 

80.0 cc-mm/m²-24hr-atm
@Thickness 0.0254 mm

203 cc-mil/100 in²-24hr-atm
@Thickness 0.00100 in

3150 cc/m²-24hr-bar; film; b.o. ISO 2556

80.0 cc-mm/m²-24hr-atm
@Thickness 0.100 mm

203 cc-mil/100 in²-24hr-atm
@Thickness 0.00394 in

800 cc/m²-24hr-bar; film; b.o. ISO 2556

Nitrogen Transmission 

16.0 cc-mm/m²-24hr-atm
@Thickness 0.100 mm

40.6 cc-mil/100 in²-24hr-atm
@Thickness 0.00394 in

160 cc/m²-24hr-bar; film; b.o. ISO 2556

16.0 cc-mm/m²-24hr-atm
@Thickness 0.0254 mm

40.6 cc-mil/100 in²-24hr-atm
@Thickness 0.00100 in

630 cc/m²-24hr-bar; film; b.o. ISO 2556

Carbon Dioxide Transmission 

480 cc-mm/m²-24hr-atm
@Thickness 0.0254 mm

1220 cc-mil/100 in²-24hr-atm
@Thickness 0.00100 in

18900 cc/m²-24hr-bar; film; b.o. ISO 2556

480 cc-mm/m²-24hr-atm
@Thickness 0.100 mm

1220 cc-mil/100 in²-24hr-atm
@Thickness 0.00394 in

4800 cc/m²-24hr-bar; film; b.o. ISO 2556

Linear Mold Shrinkage, Flow 

0.0065 cm/cm
@Thickness 2.00 mm

0.0065 in/in
@Thickness 0.0787 in

60x60x2 mm; 500 bar; ISO 294-4

Linear Mold Shrinkage, Transverse 

0.0065 cm/cm
@Thickness 2.00 mm

0.0065 in/in
@Thickness 0.0787 in

60x60x2 mm; 500 bar; ISO 294-4

Melt Flow 

20 g/10 min
@Load 1.20 kg,
Temperature 300 °C

20 g/10 min
@Load 2.65 lb,
Temperature 572 °F

ISO 1133

Mechanical Properties

Metric

English

Comments

Puncture Resistance 

5100 N
@Temperature 23.0 °C

1150 lb (f)
@Temperature 73.4 °F

ISO 6603-2

6000 N
@Temperature -30.0 °C

1350 lb (f)
@Temperature -22.0 °F

ISO 6603-2

Ball Indentation Hardness 

113 MPa

16400 psi

ISO 2039-1

Tensile Strength at Break 

70.0 MPa

10200 psi

50 mm/min; ISO 527-1,-2