Material Notes:
HF0961 is a pelleted high molecular weight, high density polyethylene Hexene-1 resin for tubular film extrusion.Applications: Grocery sacks, shopping bags, liners notion and millinery bags.Advantages: High extrusion rate with high film strength and rigidity, excellent drawdown for high quality thin film.Information provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
| Base Resin Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Thickness | 17.0 microns | 0.669 mil | extruded at 4:1 BUR |
| Base Resin Melt Index | 0.10 g/10 min | 0.10 g/10 min | I<sub>2</sub>; ASTM D1238 |
| 11 g/10 min | 11 g/10 min | I<sub>21</sub>; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.400 g/micron | 10.2 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.00 g/micron | 76.2 g/mil | ASTM D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 58.8 MPa | 8530 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.1 MPa | 6400 psi | ASTM D882 |
| 1% Secant Modulus, MD | 1176.8 MPa | 170680 psi | ASTM D882 |
| 1% Secant Modulus, TD | 1280 MPa | 185000 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 – 240 °C | 356 – 464 °F | |
| Blow-up Ratio (BUR) | 4.0 | 4.0 | |
Specification: HD HM-TITAN-HF0961
|
User Reviews
Be the first to review “HD HM-TITAN-HF0961”
- 1%
ABS-LG-AF312A-Flame Retardant
Sold by Natraj
Original price was: ₹3,500.00.₹3,450.00Current price is: ₹3,450.00.
Min (200 piece)
There are no reviews yet.