Product Description
HTA 001HP5 is a high molecular weight HDPE film grade providing very good processability on high output extruders. Films made from HTA 001HP5 exhibit excellent impact and toughness properties as well as high stiffness.
General | |||||
Availability 1 | • Africa & Middle East | • Asia Pacific | • Europe | ||
Additive | • Antiblock: No | • Slip: No | • Thermal Stabilizer: Yes | ||
Applications | • Blown Film
• Grocery Sacks |
• Liners
• Refuse Bags |
• Shoppers
• Thin Gauged Consumer Bags |
||
Revision Date | • 09/15/2016 | ||||
Resin Properties | Typical Value | (English) | Typical Value | (SI) Test Based On | |
Density | 0.952 | g/cm³ | 0.952 | g/cm³ ASTM D1505 | |
High Load Melt Index (190°C/21.6 kg) | 9.5 | g/10 min | 9.5 | g/10 min ASTM D1238 | |
Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.32 | g/10 min | 0.32 | g/10 min ASTM D1238 | |
Thermal | Typical Value | (English) | Typical Value | (SI) Test Based On | |
Vicat Softening Temperature | 259 | °F | 126 | °C ASTM D1525 | |
Film Properties | Typical Value | (English) | Typical Value | (SI) Test Based On | |
Tensile Strength at Yield MD | 5900 | psi | 41 | MPa ASTM D882 | |
Tensile Strength at Yield TD | 4200 | psi | 29 | MPa ASTM D882 | |
Tensile Strength at Break MD | 8300 | psi | 60 | MPa ASTM D882 | |
Tensile Strength at Break TD | 7000 | psi | 48 | MPa ASTM D882 | |
Elongation at Break MD | 210 | % | 210 | % ASTM D882 | |
Elongation at Break TD | 430 | % | 430 | % ASTM D882 | |
Secant Modulus MD – 1% Secant | 170000 | psi | 1200 | MPa ASTM D882 | |
Secant Modulus TD – 1% Secant | 170000 | psi | 1200 | MPa ASTM D882 | |
Dart Drop Impact | 190 | g | 190 | g ASTM D1709A | |
Elmendorf Tear Strength MD | 7 | g | 7 | g ASTM D1922 | |
Elmendorf Tear Strength TD | 30 | g | 30 | g ASTM D1922 |
Specification: HD HM-ExxonMobil-HTA001HP5
|
User Reviews
Be the first to review “HD HM-ExxonMobil-HTA001HP5”
Vendor Information
- Store Name: Natraj
- Vendor: Natraj
-
Address:
A-250, Narela Industrial Area
110040
Delhi - No ratings found yet!
There are no reviews yet.