Good release property DuPont pom 500AF pellets pom plastic Particles virgin material granules

Physical Properties

Metric

English

Comments

Density 

1.53 g/cc

0.0553 lb/in³

ISO 1183

Melt Density 

1.28 g/cc
@Temperature 215 °C

0.0462 lb/in³
@Temperature 419 °F

Water Absorption 

0.25 %
@Time 86400 sec

0.25 %
@Time 24.0 hour

Immersion; Sim. to ISO 62

1.0 %
@Thickness 2.00 mm

1.0 %
@Thickness 0.0787 in

Sim. to ISO 62

Moisture Absorption 

0.200 %
@Thickness 2.00 mm

0.200 %
@Thickness 0.0787 in

Sim. to ISO 62

Linear Mold Shrinkage, Flow 

0.020 cm/cm

0.020 in/in

ISO 294-4, 2577

Linear Mold Shrinkage, Transverse 

0.014 cm/cm

0.014 in/in

ISO 294-4, 2577

Melt Flow 

5.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C

5.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F

ISO 1133

Mechanical Properties

Metric

English

Comments

Hardness, Rockwell M 

74

74

ISO 2039-2

Hardness, Rockwell R 

119

119

ISO 2039-2

Tensile Strength at Break 

50.0 MPa

7250 psi

ISO 527-1/-2

Elongation at Break 

10 %

10 %

ISO 527-1/-2

Tensile Modulus 

2.80 GPa

406 ksi

ISO 527-1/-2

Flexural Modulus 

2.50 GPa

363 ksi

ISO 178

Compressive Strength 

110 MPa

16000 psi

ISO 604

Poissons Ratio 

0.37

0.37

Izod Impact, Notched (ISO) 

3.00 kJ/m²
@Temperature 23.0 °C

1.43 ft-lb/in²
@Temperature 73.4 °F

ISO 180/1A

Charpy Impact Unnotched 

3.50 J/cm²
@Temperature -30.0 °C

16.7 ft-lb/in²
@Temperature -22.0 °F

ISO 179/1eU

4.00 J/cm²
@Temperature 23.0 °C

19.0 ft-lb/in²
@Temperature 73.4 °F

ISO 179/1eU

Charpy Impact, Notched 

0.300 J/cm²
@Temperature -30.0 °C

1.43 ft-lb/in²
@Temperature -22.0 °F

ISO 179/1eA

0.300 J/cm²
@Temperature 23.0 °C

1.43 ft-lb/in²
@Temperature 73.4 °F

ISO 179/1eA