Greenflex ML 50 F is an ethylene vinyl acetate copolymer (EVA) for injection moulding, compounding and extrusion.
Main Application
Greenflex ML 50 F is recommended for the production of foamed and crosslinked sheets for shoes, dolls, shock absorbers and gasket.
| Resin Properties | Value | Unit | Test Method |
| Melt Flow Rate (190 °C/2.16 kg) | 2.5 | g/10min | ISO 1133 |
| Vinyl acetate content | 19 | % | Internal method |
| Density | 0.941 | g/cm3 | ISO 1183 |
| Melting Point | 83 | °C | Internal method |
| Brittleness temperature | <- 80 | °C | ASTM D 746 |
| Vicat softening point (1 kg) | 58 | °C | ISO 306/A |
| Mechanical Properties * | Value | Unit | Test Method |
| Tensile stress at yield | 4.5 | MPa | ISO 527 |
| Tensile stress at break | – | MPa | ISO 527 |
| Elongation at break | – | % | ISO 527 |
| Flexural modulus | 40 | MPa | ISO 178 |
| Hardness Shore A | 89 | – | ISO 868 A |
| Hardness Shore D | 36 | – | ISO 868 A |
Specification: EVA-18% TO 25%-GREENFLEX-ML50F
|