Repol H110FG is recommended for Staple Fibres & Continuous High Tenacity Filaments. The grade is specially formulated for Anti gas fading stability. Repol H110FG is an ideal material for spinning of fine denier staple fibres.
Typical Characteristics |
Property |
Test Method |
Unit |
Typical Value * |
Melt Flow Rate, (230°C / 2.16kg) |
ASTM D1238 |
g/10min |
9.0 |
Tensile Strength at Yield (50mm/min) |
ASTM D638 |
MPa |
35 |
Elongation at Yield (50mm/min) |
ASTM D638 |
% |
8 |
Flexural Modulus (1% secant ) |
ASTM D790A |
MPa |
1600 |
Notched Izod Impact strength (23°C) |
ASTM D256 |
J/m |
30 |
Heat Deflection Temperature (455 kPa) |
ASTM D648 |
°C |
104 |