Luban polypropylene is manufactured using Novolen vertical stirred Gas-phase polymerization process. Luban HP5101LC is a homopolymer polypropylene which has a narrow molecular weight distribution with anti-gas fading stabilization.
Application
High tenacity staple fibers, suitable for extrusion of staple fibers, geotextiles.
Properties (Typical Values)
| Property | Units | Test method | Value |
| Melt flow rate (230°C/2.16 kg) | g/10 min | ISO 1133 | 5 |
| Density | g /cm³ | ISO 1183 | 0.90 |
| Tensile modulus (1 mm/min) | MPa | ISO 527-2 | 1550 |
| Tensile stress at yield (50 mm/min) | MPa | ISO 527-2 | 35 |
| Tensile strain at yield (50 mm/min) | % | ISO 527-2 | 8 |
| Tensile strain at break (50 mm/min) | % | ISO 527-2 | > 50 |
| Charpy unnotched impact strength (+23°C) | kJ/m² | ISO 179/1eU | 110 |
| Charpy notched impact strength (+23°C) | kJ/m² | ISO 179/1eA | 3 |
| Heat Deflection Temperature (0.45 MPa) | °C | ISO 75-2 | 85 |
Specification: PP RAFFIA-LUBAN-HP5101LC
|